Additive manufacturing technologies allow producing a regular three-dimensional mesh of interconnected struts that form an open-cell porous structure. Regular porous structures have been used in the orthopedic industry due to outstanding bone anchoring. The aim of the study was to determine how the postprocessing influences the mechanical properties of porous structures made of titanium alloy CL 41TI ELI. The effect of hot isostatic pressing (HIP) as a method of increasing microstructural integrity was investigated here. The influence of surface etching (SE) technique, which was applied to the porous structure for cleaning unmelted titanium powder particles on the surface of connectors from the inner surfaces of a porous structure, was examined in this study. Mechanical properties were investigated by means of compression tests. The results point out that HIP has a minor effect on the mechanical behavior of considered porous structures. The SE is an effective method to clean the surface of a porous structure, which is very important in the case of biomedical applications when loose powder can cause serious health problems. Another effect of the SE is also the strut thickness reduction. Reducing strut thickness of a porous structure with the surface etching decreases its stiffness to the same extent as predicted by the relative density theoretical model but did not result in structural damage.

Department of Mechanics Biomechanics and Mechatronics Faculty of Mechanical Engineering Czech Technical Universityin Prague Technická 1902 4 16000 Prague Czech Republic

Department of Metals and Corrosion Engineering University of Chemistry and Technology Technická 5 16628 Prague Czech Republic

Mechanical Testing and Thermophysical Measurement Department COMTES FHT a s Průmyslová 995 33441 Dobrany Czech Republic

Citace poskytuje Crossref.org