The aim of this study was to test C/C material (carbonized, graphitized or covered with pyrolytic carbon) designated for the use in orthopaedic and bone surgery. Using an in vitro assay we confirmed, that the cell proliferation was exhibited the mostly on the C/C composite coated with pyrolitic carbon and afterwards polished. The two latest of subsequent water extracts of this material had a slightly inhibiting effect on the cells metabolic activity. Biocompatibility test in vivo performed subcutaneously on rats did not show big differences between three tested implants (C/C composite, epoxy resine, titanium alloy), on the other hand the plates tested on pigs demonstrated foreign-body reaction induced by wear C/C composite material. Such debris were found both in the neighborhood of the implant as well as in the lymphatic node.

Rheumatism Institute Na Slupi 4 Prague 2 12850 Czech Republic

Zobrazit více v PubMed

Biomaterials. 1992;13(9):646-8 PubMed

Acta Chir Orthop Traumatol Cech. 1992;59(5):302-4 PubMed

J Mater Sci Mater Med. 1998 Dec;9(12):773-7 PubMed

Orthop Rev. 1988 Apr;17(4):402-7 PubMed

J Long Term Eff Med Implants. 1995;5(3):209-31 PubMed

Anal Biochem. 1984 Aug 1;140(2):417-23 PubMed

J Biomed Mater Res. 1996 Apr;30(4):523-33 PubMed

The influence of implant surface properties on cell adhesion and proliferation

Biological properties of the intervertebral cages made of titanium containing a carbon-carbon composite covered with different polymers

Biological and biochemical properties of the carbon composite and polyethylene implant materials