Three new calcium phenylphosphonates, CaC(6)H(5)PO(3).2H(2)O, Ca(3)(C(6)H(5)PO(3)H)(2)(C(6)H(5)PO(3))(2).4H(2)O, and CaC(6)H(5)PO(3).H(2)O, and two calcium 4-carboxyphenylphosphonates, Ca(HOOCC(6)H(4)PO(3)H)(2) and Ca(3)(OOCC(6)H(4)PO(3))(2).6H(2)O, were prepared. It was found that CaC(6)H(5)PO(3).2H(2)O transformed into previously known Ca(C(6)H(5)PO(3)H)(2) via Ca(3)(C(6)H(5)PO(3)H)(2)(C(6)H(5)PO(3))(2).4H(2)O in the presence of phenylphosphonic acid, and vice versa, Ca(C(6)H(5)PO(3)H)(2) turned into CaC(6)H(5)PO(3).2H(2)O in a weak basic medium. A similar relationship was found between Ca(HOOCC(6)H(4)PO(3)H)(2) and Ca(3)(OOCC(6)H(4)PO(3))(2).6H(2)O; i.e., Ca(3)(OOCC(6)H(4)PO(3))(2).6H(2)O transformed into Ca(HOOCC(6)H(4)PO(3)H)(2) in the presence of 4-carboxyphenylphosphonic acid. On the contrary, Ca(3)(OOCC(6)H(4)PO(3))(2).6H(2)O is formed from Ca(HOOCC(6)H(4)PO(3)H)(2) in the presence of ammonium as a weak base. The structure of Ca(HOOCC(6)H(4)PO(3)H)(2) was solved from X-ray powder diffraction data by an ab initio method using a FOX program. The compound is monoclinic, space group C2/c (No. 15), a = 49.218(3) A, b = 7.7609(4) A, c = 5.4452(3) A, beta = 128.119(3) degrees , and Z = 4. Its structure is one-dimensional with [Ca(2)(HOOCC(6)H(4)PO(3)H)(4)](infinity) ribbons forming basic building blocks. The ribbons are held together by hydrogen bonds between carboxylic groups.

Joint Laboratory of Solid State Chemistry of the Institute of Macromolecular Chemistry of Academy of Sciences and University of Pardubice Studentská 84 532 10 Pardubice Czech Republic

Citace poskytuje Crossref.org

Synthesis and Exfoliation of Calcium Organophosphonates for Tailoring Rheological Properties of Sodium Alginate Solutions: A Path toward Polysaccharide-Based Bioink

Layered calcium phenylphosphonate: a hybrid material for a new generation of nanofillers

Influence of 1,2-alkanediols on the structure of their intercalates with strontium phenylphosphonate solved by molecular simulation and experimental methods