Thermoresponsive nanoparticles based on the interaction of metallacarboranes, bulky chaotropic and surface-active anions, and poly(2-alkyl-2-oxazoline) block copolymers were prepared. Recently, the great potential of metallacarboranes have been recognized in biomedicine and many delivery nanosystems have been proposed. However, none of them are thermoresponsive. Therefore, a thermoresponsive block copolymer, poly(2-methyl-2-oxazoline)-block-poly(2-n-propyl-2-oxazoline) (PMeOx-PPrOx), was synthesized to encapsulate metallacarboranes. Light scattering, NMR spectroscopy, isothermal titration calorimetry, and cryogenic TEM were used to characterize all solutions of the formed nanoparticles. The cloud-point temperature (TCP ) of the block copolymer was observed at 30 °C and polymeric micelles formed above this temperature. Cobalt bis(dicarbollide) anion (COSAN) interacts with both polymeric segments. Depending on the COSAN concentration, this affinity influenced the phase transition of the thermoresponsive PPrOx block. The TCP shifted to lower values at a lower COSAN content. At higher COSAN concentrations, the hybrid nanoparticles are fragmented into relatively small pieces. This system is also thermoresponsive, whereby an increase in temperature leads to higher polymer mobility and COSAN release.

Department of Physical and Macromolecular Chemistry Faculty of Science Charles University Hlavova 2030 128 40 Prague 2 Czech Republic

Institute of Biology and Medical Genetics 1st Faculty of Medicine Charles University and General University Hospital Prague Purkynie Ustav Albertov 4 12 801 Prague Czech Republic

Supramolecular Chemistry Group Department of Organic and Macromolecular chemistry Faculty of Sciences Ghent University Krijgslaan 281 S4 B 9000 Gent Belgium

Citace poskytuje Crossref.org

Effect of Dexamethasone on Thermoresponsive Behavior of Poly(2-Oxazoline) Diblock Copolymers