The traditional Japanese method of wood surface charring was studied. To perform the surface charring, three sawn Norway spruce and Silver fir wood boards of dimension 190 × 24 × 4000 mm3 were tied together to act as a chimney and charred in a short time (3-4 min) with open flame at a temperature above 500 °C. Temperature inside the chimney was recorded on the three different positions during the charring process. Surface temperature of spruce increased from 0 °C to 500 °C in approx. 120-300 s while fir increased in approx. 100-250 s. The thickness of the charred layer and the resulting cupping effect were investigated at the different heights of the chimney to evaluate its variability. Temperature achieved during the charring process was sufficient to get a significant charred layer of 2.5 and 4.5 mm on average for spruce and fir samples, respectively. The analyzed samples showed a significant cupping effect to the charred side with no difference between the annual ring orientation of sawn boards. Spruce exhibit a more significant cupping effect when compared to fir, i.e., 3.2-6 mm and 2.2-4.5 mm, respectively. Furthermore, the pH values of charred samples increased significantly, which could be an indication of improved resistance against wood-decay fungi. For better insight into the traditional charring method, further studies should be carried out to execute the charring process in a consistent quality and therefore fully exploit its potential.

Department of Wood Science and Technology Faculty of Forestry and Wood Technology Mendel University in Brno Zemědělská 3 613 00 Brno Czech Republic

Faculty for Design of Furniture and Wood Engineering Transilvania University of Brasov B dul Eroilor nr 29 500036 Brasov Romania

Forest Products Technology and Timber Construction Salzburg University of Applied Sciences Markt 136a 5431 Kuchl Austria

Zobrazit více v PubMed

Jones D., Brischke C. Performance of Bio-Based Building Materials. Woodhead Publishing; Duxforf, UK: 2017.

Hill C. Wood Modification: Chemical, Thermal and Other Processes. John Wiley & Sons, Ltd.; West Sussex, UK: 2006.

Sandberg D., Kutnar A., Mantanis G. Wood modification technologies—A review. iForest Biogeosci. For. 2017;10:895–908. doi: 10.3832/ifor2380-010. DOI

Kymäläinen M., Hautamäki S., Lillqvist K., Segerholm K., Rautkari L. Surface modification of solid wood by charring. J. Mater. Sci. 2017;52:6111–6119. doi: 10.1007/s10853-017-0850-y. DOI

Čermák P., Dejmal A., Paschova Z., Kymäläinen M., Dömény J., Brabec M., Hess D., Rautkari L. One-sided surface charring of beech wood. J. Mater. Sci. 2019;54:9497–9506. doi: 10.1007/s10853-019-03589-3. DOI

Kymäläinen M., Turunen H., Rautkari L. Effect of Weathering on Surface Functional Groups of Charred Norway Spruce Cladding Panels. Forests. 2020;11:1373. doi: 10.3390/f11121373. DOI

Kymäläinen M., Turunen H., Čermák P., Hautamäki S., Rautkari L. Sorption-Related Characteristics of Surface Charred Spruce Wood. Materials. 2018;11:2083. doi: 10.3390/ma11112083. PubMed DOI PMC

Gosselink R., Krosse A., van der Putten J., van der Kolk J., Klerk-Engels B., van Dam J. Wood preservation by low-temperature carbonisation. Ind. Crop. Prod. 2004;19:3–12. doi: 10.1016/S0926-6690(03)00037-2. DOI

Fengel D., Wegener G. Wood: Chemistry, Ultrastructure, Reactions. Walter de Gruyter; New York, NY, USA: 1989.

White R., Dietenberger M. Encyclopedia of Materials: Science and Technology. Elsevier Science Ltd.; Amsterdam, The Netherlands: 2001. Wood products: Thermal degradation and fire; pp. 9712–9716.

Shafizadeh F. The chemistry of pyrolysis and combustion. In: Rowell R., editor. The Chemistry of Solid Wood. American Chemical Society; Washington, DC, USA: 1984. pp. 489–530. (Advances in Chemistry Series 207).

Beall F.C., Eickner H.W. USDA Forest Service Research. University of Minnesota; Minneapolis, MN, USA: 1970. Thermal degradation of wood components: A review of the literature. Paper FPL130.

Stelzer R. Oberflächliches Verkohlen von Schittholz für Einen Langanhaltenden Außen-und Inneneinsatz. Masterarbeit, Fachhochschule Salzburg; Salzburg, Kuchl: 2017.

Suleiman B.M., Larfeldt J., Leckner B., Gustavsson M. Thermal conductivity and diffusivity of wood. Wood Sci. Technol. 1999;33:465–473. doi: 10.1007/s002260050130. DOI

Boonstra M.J., Rijsdijk J.F., Sander C., Kegel E., Tjeerdsma B., Militz H., Van Acker J., Stevens M. Microstructural and physical aspects of heat-treated wood. Part 1. Softwoods. Maderas. Cienc. Y Tecnol. 2006;8:193–208.

Virta J. Wooden cladding boards in cyclic moisture conditions: Studies of cupping, moisture distribution and swelling stress. Build. Environ. 2005;40:1395–1399. doi: 10.1016/j.buildenv.2004.10.014. DOI

Niemz P., Sonderegger W. Holzphysik: Physik des Holzes und der Holzwerkstoffe. Carl Hanser Verlag Gmbh & Co KG; Leipzig, Germany: 2017.

Paulitsch M., Barbu M. Holzwerkstoffe der Moderne. DRW-Verlag; Leinfelden-Echterdingen, Germany: 2015.

Wagenführ R. Holzatlas. Fachbuchverlag; Leipzig, Germany: 2007.

Weber K., Quicker P. Properties of biochar. Fuel. 2018;217:240–261. doi: 10.1016/j.fuel.2017.12.054. DOI