OBJECTIVES: The objective of this study was to observe and to measure the impact of corundum sandblasting on the thickness of the Immediate dentin sealing layer. METHODS: 20 recently extracted molars were collected and divided randomly into two groups. A standardized preparation was performed on each tooth and the Optibond FL dentin bonding agent (Kerr, Orange, USA) was applied on the prepared surface according to the manufacturer’s instructions. The surface was then partially sandblasted. RONDOflex plus 360 (KaVo, Bieberach an der Riss, Germany) and Airsonic Mini-Sandblaster (Hager et Werken, Duisburg, Germany) were used. Microscope observations were made. RESULTS: The arithmetic mean of the Optibond FL dentin bonding agent film thickness was 48.72 μm (Group 1=45.55 μm and Group 2=51.88 μm). The dentin bonding agent layer thickness was reduced to the average value of 17,12 μm by RONDOflex plus 360 sandblasting (Group 1). The zero value was recorded in 16 % of the locations. The Airsonic Mini-Sandblaster sandblasting changed the average thickness of the dentin bonding agent layer to 13.25 μm with 31 % of zero values (Group 2). CONCLUSION: The results of this research lead to a reflection on modifications of the immediate dentin sealing procedure (Tab. 4, Fig. 3, Ref. 28).
- MeSH
- dentinová adheziva * klasifikace MeSH
- lidé MeSH
- mikroskopie MeSH
- moláry účinky léků MeSH
- oxid hlinitý MeSH
- pískování zubů * metody MeSH
- statistika jako téma MeSH
- zubní sklovina diagnostické zobrazování účinky léků MeSH
- Check Tag
- lidé MeSH
- Publikační typ
- pozorovací studie MeSH
- práce podpořená grantem MeSH
Úvod a cíl: V posledních letech přibývá v ordinacích zubních lékařů pacientů s vývojovým postižením skloviny u molárů a řezáků. Jedná se o onemocnění systémového původu postihující jeden až čtyři první stálé moláry, které je často spojené s poškozením stálých řezáků. Toto onemocnění nemá zcela objasněnou etiologii. V literatuře jsou zmíněny vlivy vnějšího prostředí, v úvahu je třeba brát i vlivy genetické. U těchto pacientů nahrazujeme ztracené tvrdé zubní tkáně molárů, ale také zlepšujeme estetiku řezáků, na kterých se mohou nacházet opacity pokrývající téměř celou vestibulární plošku. Při volbě terapie se rozhodujeme na základě stavu chrupu, spolupráce a věku pacienta. Ke každému pacientovi musíme přistupovat individuálně a zvolit pro něj vhodnou terapii. Cílem tohoto článku je shrnout dostupné informace o etiopatogenezi, klasifikaci, histologických změnách, klinickém obrazu, prevenci a terapii molárové a řezákové hypomineralizace. Metodika: Pro tento přehledový článek byly využity odborné publikace z databází PubMed a Web of Science. Publikace byly vyhledávány v anglickém jazyce za pomoci klíčových slov: MIH, molár, řezák, molárová a řezáková hypomineralizace, DDE, hypomineralizace, opacita. Jako zdroje pro tento přehled byly využity články publikované mezi lety 2006 a 2021. Závěr: U molárové a řezákové hypomineralizace je důležitá včasná diagnostika a zavedení preventivních postupů tak, abychom zamezili možným komplikacím souvisejícím s tímto onemocněním. Navíc prevalence tohoto onemocnění v populaci narůstá a s pacienty postiženými molárovou a řezákovou hypomineralizací se setkáváme stále častěji.
Introduction, aim: The number of patients with affected enamel in molar incisor hypomineralization is increasing in the dental offices in recent years. It is a hypomineralization of systemic origin affecting at least one first permanent molar, often associated with affected permanent incisors. The etiology of this disease is not fully understood. The literature mentions influences of external environment and contemplates genetic factors. We reconstruct the hard dental tissues loss of permanent molars and improve the aesthetics of incisors in these cases. The therapy is based on the condition of the teeth, cooperation and age of the patient. We must approach each patient individually and choose the appropriate therapy for them. The aim of this article is to summarize the available information on etiopathogenesis, classification, histological changes and clinical picture, prevention and therapy of molar incisor hypomineralization. Methods: The PubMed and Web of Science databases were used to gather articles for this review. The publications were searched in English language using the key words: MIH, molar, incisor, molar incisor hypomineralization, DDE, hypomineralization, opacity. Articles published between 2006 and 2021 were used as sources for this review. Conclusions: Early diagnosis and implementation of preventive procedures are important to avoid possible complications related to molar incisor hypomineralization. Moreover, the prevalence of this desease in the population is increasing and patients affected by molar incisor hypomineralization are more frequently encountered in the dental office.
- Publikační typ
- abstrakt z konference MeSH
Úvod a cíl: Zirkoniová keramika je aktuálně nejpoužívanějším zástupcem polykrystalických dentálních keramik. Je vysoce ceněna pro svoje mechanické vlastnosti: tvrdost, pevnost a houževnatost. Naopak jako nedostatek zirkoniové keramiky je vnímána její estetika. Její nedostatečná transparence znemožňuje napodobení optických vlastností skloviny, a proto je její indikace v monolitické formě často omezena pouze na laterální úseky. Tento článek pojednává o vlastnostech zirkoniové keramiky a o jejím vývoji. Zvláštní důraz je kladen na chemicko-fyzikální podstatu jevů, které se podílejí na determinaci vlastností zirkoniové keramiky, jako jsou její krystalická struktura, složení, její stabilita případně metastabilita, a dále na omezení indikací jednotlivých generací zirkoniové keramiky. Závěr: Ekonomický potenciál zirkoniové keramiky se ukazuje jako silný stimulant jejího vývoje. Estetické nedostatky materiálu byly největším omezujícím faktorem pro jeho širší využití. Nejprostším a nejstarším řešením této problematiky se stalo fazetování zirkoniové keramiky pomocí keramiky s vysokým obsahem skla. U této kombinace materiálů byl ovšem zjištěn relativně častý výskyt komplikací spojených s odlamováním povrchových vrstev fazety. Nejvýhodnějším z pohledu mechaniky se ukázalo být využití zirkoniové keramiky v monolitické formě. Proto se vývoj zirkoniové keramiky v posledních deseti letech vydal směrem zvyšování transparence zirkoniové keramiky samotné. Výsledkem těchto snah se stala poslední generace zirkoniové keramiky, která má podstatně zlepšenou estetiku a lze ji využít i v oblastech relativně esteticky exponovaných. Tyto nové materiály si uchovávají pouze část mechanické odolnosti svých předchůdců, a proto jsou jejich indikace omezeny pouze na tříčlenné můstky. Stále však výrazně rozšiřují portfolio možností využití monolitické zirkoniové keramiky a stávají se vhodnou alternativou ke starším materiálům používaným pro zhotovení korunek a můstků.
Introduction and aim: Zirconia is currently the most commonly used representative of polycrystalline dental ceramics. It is highly valued for its mechanical properties: hardness, strength and toughness. On the contrary, its aesthetics is percieved as a disadvantage. Its insufficient transparency makes it impossible to mimic the optical properties of enamel, and therefore its indication in monolithic form is often limited to distal sections only. This article discusses the properties of zirconia ceramics and its evolution. Particular emphasis is placed on the chemical-physical nature of the phenomena involved in determining the properties of dental zirconia. Conclusion: The economic potential of zirconia ceramics is proving to be a strong stimulant of its development. The aesthetic disadvantages of the material were the biggest limiting factor for its wider use. The simplest and earliest solution to this problem was the veneering of zirconia using high glass content ceramics. This combination of materials, however, was found to have relatively frequent complications associated with chipping of the surface layers of the veneer. The use of zirconia ceramics in monolithic form proved to be the most advantageous from a mechanical point of view. Therefore, the development of zirconia ceramics in the last ten years has gone in the direction of increasing the transparency of the zirconia ceramic itself. The result of these efforts has been the latest generation of zirconia ceramics, which have significantly improved aesthetics and can be used even in relatively aesthetically exposed areas. These new materials retain only a fraction of the mechanical durability of their predecessors, and therefore their indications are limited to three-unit bridges. However, they still significantly expand the portfolio of applications for monolithic zirconia ceramics and are becoming a suitable alternative to older materials used for crown and bridge fabrication.
- Publikační typ
- abstrakt z konference MeSH