Nanomechanical characterization of alumina coatings grown on FeCrAl alloy by thermal oxidation

E. Frutos, JL. González-Carrasco, T. Polcar,

. 2016 ; 57 (-) : 310-20. [pub] 20160201

Language English Country Netherlands

Document type Journal Article, Research Support, Non-U.S. Gov't

Persistent link   https://www.medvik.cz/link/bmc17000477

This work studies the feasibility of using repetitive-nano-impact tests with a cube-corner tip and low loads for obtaining quantitative fracture toughness values in thin and brittle coatings. For this purpose, it will be assumed that the impacts are able to produce a cracking, similar to the pattern developed for the classical fracture toughness tests in bulk materials, and therefore, from the crack developed in the repetitive impacts it will be possible to evaluate the suitability of the classical indentation models (Anstins and Laugier) for measuring fracture toughness. However, the length of this crack has to be lower than 10% of the total coating thickness to avoid substrate contributions. For this reason, and in order to ensure a small plastic region localized at the origin of the crack tip, low load values (or small distance between the indenter tip and the surface) have to be used. In order to demonstrate the validity of this technique, repetitive-nano-impact will be done in a fine and dense oxide layer (α-Al2O3), which has been developed on the top of oxide dispersion strengthened (ODS) FeCrAl alloys (PM 2000) by thermal oxidation at elevated temperatures. Moreover, it will be shown how it is possible to know with each new impact the crack geometry evolution from Palmqvist crack to half-penny crack, being able to study the proper evolution of the different values of fracture toughness in terms of both indentation models and as a function of the strain rate, ε̇, decreasing. Thereby, fracture toughness values for α-Al2O3 layer decrease from ~4.40MPam , for high ϵ̇ value (10(3)s(-1)), to ~3.21MPam, for quasi-static ϵ̇ value (10(-3)s(-1)). On the other hand, ϵ̇ a new process to obtain fracture toughness values will be analysed, when the classical indentation models are not met. These values are typically found in the literature for bulk α-Al2O3, demonstrating the use of repetitive-nano-impact tests which not only provide qualitative information about fracture resistance of the materials but it also can be used to obtain quantitative information as fracture toughness values in the case of brittle materials.

References provided by Crossref.org

000      
00000naa a2200000 a 4500
001      
bmc17000477
003      
CZ-PrNML
005      
20170119100747.0
007      
ta
008      
170103s2016 ne f 000 0|eng||
009      
AR
024    7_
$a 10.1016/j.jmbbm.2016.01.027 $2 doi
024    7_
$a 10.1016/j.jmbbm.2016.01.027 $2 doi
035    __
$a (PubMed)26875145
040    __
$a ABA008 $b cze $d ABA008 $e AACR2
041    0_
$a eng
044    __
$a ne
100    1_
$a Frutos, E $u Department of Control Engineering, Faculty of Electrical Engineering, Czech Technical University in Prague, Technická 2, Prague 6, 16627, Czech Republic. Electronic address: frutoemi@fel.cvut.cz.
245    10
$a Nanomechanical characterization of alumina coatings grown on FeCrAl alloy by thermal oxidation / $c E. Frutos, JL. González-Carrasco, T. Polcar,
520    9_
$a This work studies the feasibility of using repetitive-nano-impact tests with a cube-corner tip and low loads for obtaining quantitative fracture toughness values in thin and brittle coatings. For this purpose, it will be assumed that the impacts are able to produce a cracking, similar to the pattern developed for the classical fracture toughness tests in bulk materials, and therefore, from the crack developed in the repetitive impacts it will be possible to evaluate the suitability of the classical indentation models (Anstins and Laugier) for measuring fracture toughness. However, the length of this crack has to be lower than 10% of the total coating thickness to avoid substrate contributions. For this reason, and in order to ensure a small plastic region localized at the origin of the crack tip, low load values (or small distance between the indenter tip and the surface) have to be used. In order to demonstrate the validity of this technique, repetitive-nano-impact will be done in a fine and dense oxide layer (α-Al2O3), which has been developed on the top of oxide dispersion strengthened (ODS) FeCrAl alloys (PM 2000) by thermal oxidation at elevated temperatures. Moreover, it will be shown how it is possible to know with each new impact the crack geometry evolution from Palmqvist crack to half-penny crack, being able to study the proper evolution of the different values of fracture toughness in terms of both indentation models and as a function of the strain rate, ε̇, decreasing. Thereby, fracture toughness values for α-Al2O3 layer decrease from ~4.40MPam , for high ϵ̇ value (10(3)s(-1)), to ~3.21MPam, for quasi-static ϵ̇ value (10(-3)s(-1)). On the other hand, ϵ̇ a new process to obtain fracture toughness values will be analysed, when the classical indentation models are not met. These values are typically found in the literature for bulk α-Al2O3, demonstrating the use of repetitive-nano-impact tests which not only provide qualitative information about fracture resistance of the materials but it also can be used to obtain quantitative information as fracture toughness values in the case of brittle materials.
650    _2
$a slitiny $x chemie $7 D000497
650    _2
$a oxid hlinitý $x chemie $7 D000537
650    12
$a testování materiálů $7 D008422
650    12
$a mechanické jevy $7 D055595
650    12
$a nanotechnologie $7 D036103
650    _2
$a oxidace-redukce $7 D010084
650    _2
$a mechanický stres $7 D013314
650    12
$a teplota $7 D013696
655    _2
$a časopisecké články $7 D016428
655    _2
$a práce podpořená grantem $7 D013485
700    1_
$a González-Carrasco, J L $u Centro Nacional de Investigaciones Metalúrgicas, CENIM-CSIC, Avda. Gregorio del Amo 8, 28040 Madrid, Spain; Centro de Investigación Biomédica en Red de Bioingeniería, Biomateriales y Nanomedicina CIBER-BBN, Spain.
700    1_
$a Polcar, T $u Department of Control Engineering, Faculty of Electrical Engineering, Czech Technical University in Prague, Technická 2, Prague 6, 16627, Czech Republic; National Centre for Advanced Tribology (nCATS), University of Southampton, University Road, Southampton SO17 1BJ, UK.
773    0_
$w MED00166961 $t Journal of the mechanical behavior of biomedical materials $x 1878-0180 $g Roč. 57, č. - (2016), s. 310-20
856    41
$u https://pubmed.ncbi.nlm.nih.gov/26875145 $y Pubmed
910    __
$a ABA008 $b sig $c sign $y a $z 0
990    __
$a 20170103 $b ABA008
991    __
$a 20170119100856 $b ABA008
999    __
$a ok $b bmc $g 1179617 $s 961044
BAS    __
$a 3
BAS    __
$a PreBMC
BMC    __
$a 2016 $b 57 $c - $d 310-20 $e 20160201 $i 1878-0180 $m Journal of the mechanical behavior of biomedical materials $n J Mech Behav Biomed Mater $x MED00166961
LZP    __
$a Pubmed-20170103

Find record

Citation metrics

Archiving options