This work deals with the mechanical characterization by depth-sensing indentation (DSI) of PLLA and PLDA composites reinforced with micro-particles of Mg (up to 15wt%), which is a challenging task since the indented volume must provide information of the bulk composite, i.e. contain enough reinforcement particles. The composites were fabricated by combining hot extrusion and compression moulding. Physico-chemical characterization by TGA and DSC indicates that Mg anticipates the thermal degradation of the polymers but does not compromise their stability during processing. Especial emphasis is devoted to determine the effect of strain rate and Mg content on mechanical behavior, thus important information about the visco-elastic behavior and time-dependent response of the composites is obtained. Relevant for the intended application is that Mg addition increases the elastic modulus and hardness of the polymeric matrices and induces a higher resistance to flow. The elastic modulus obtained by DSI experiments shows good agreement with that obtained by uniaxial compression tests. The results indicate that DSI experiments are a reliable method to calculate the modulus of polymeric composites reinforced with micro-particles. Taking into consideration the mechanical properties results, PLA/Mg composite could be used as substitute for biodegradable monolithic polymeric implants already in the market for orthopedics (freeform meshes, mini plates, screws, pins, …), craniomaxillofacial, or spine.
This work studies the feasibility of using repetitive-nano-impact tests with a cube-corner tip and low loads for obtaining quantitative fracture toughness values in thin and brittle coatings. For this purpose, it will be assumed that the impacts are able to produce a cracking, similar to the pattern developed for the classical fracture toughness tests in bulk materials, and therefore, from the crack developed in the repetitive impacts it will be possible to evaluate the suitability of the classical indentation models (Anstins and Laugier) for measuring fracture toughness. However, the length of this crack has to be lower than 10% of the total coating thickness to avoid substrate contributions. For this reason, and in order to ensure a small plastic region localized at the origin of the crack tip, low load values (or small distance between the indenter tip and the surface) have to be used. In order to demonstrate the validity of this technique, repetitive-nano-impact will be done in a fine and dense oxide layer (α-Al2O3), which has been developed on the top of oxide dispersion strengthened (ODS) FeCrAl alloys (PM 2000) by thermal oxidation at elevated temperatures. Moreover, it will be shown how it is possible to know with each new impact the crack geometry evolution from Palmqvist crack to half-penny crack, being able to study the proper evolution of the different values of fracture toughness in terms of both indentation models and as a function of the strain rate, ε̇, decreasing. Thereby, fracture toughness values for α-Al2O3 layer decrease from ~4.40MPam , for high ϵ̇ value (10(3)s(-1)), to ~3.21MPam, for quasi-static ϵ̇ value (10(-3)s(-1)). On the other hand, ϵ̇ a new process to obtain fracture toughness values will be analysed, when the classical indentation models are not met. These values are typically found in the literature for bulk α-Al2O3, demonstrating the use of repetitive-nano-impact tests which not only provide qualitative information about fracture resistance of the materials but it also can be used to obtain quantitative information as fracture toughness values in the case of brittle materials.
This aim of this study is to determine the elastoplastic properties of Ni-free Al3FeSi2 intermetallic coatings grown on medical stainless steel under different experimental conditions. Elastoplastic properties are defined by the plasticity index (PI), which correlates the hardness and the Young's modulus. Special emphasis is devoted to correlate the PI with the wear resistance under sliding contact, determined by scratch testing, and fracture toughness, determined by using a novel method based on successive impacts with small loads. With regard to the substrate, the developed coatings are harder and exhibit a lower Young's reduced modulus, irrespective of the experimental conditions. It has been shown that preheating of the samples prior to hot dipping and immersion influences the type and volume fraction of precipitates, which in turn also affect the nanomechanical properties. The higher the preheating temperature is, the greater the Young's reduced modulus is. For a given preheating condition, an increase of the immersion time yields a decrease in hardness. Although apparent friction coefficients of coated specimens are smaller than those obtained on AISI 316 LVM, they increase when using preheating or higher immersion times during processing, which correlates with the PI. The presence of precipitates produces an increase in fracture toughness, with values greater than those presented by samples processed on melted AlSi alloys with lower Si content (12 wt%). Therefore, these intermetallic coatings could be considered "hard but tough", suitable to enhance the wear resistance, especially when using short periods of immersion.