Nitric oxide sensor based on carbon fiber covered with nickel porphyrin layer deposited using optimized electropolymerization procedure

. 2007 Sep ; 71 (1) : 46-53. [epub] 20060927

Jazyk angličtina Země Nizozemsko Médium print-electronic

Typ dokumentu časopisecké články, práce podpořená grantem

Perzistentní odkaz   https://www.medvik.cz/link/pmid17084679

Electropolymerization regime of meso-tetrakis(3-methoxy-4-hydroxyphenyl) porphyrin is optimized to yield films possessing both electrocatalytical and permselective properties towards nitric oxide oxidation. The sensor composed of electrochemically oxidized carbon fiber, covered solely with nickel porphyrin derivative layer electropolymerized using our method, is characterized by high selectivity towards nitrite (1:600), ascorbate (1:8000) and dopamine (>1:80), determined by constant potential amperometry at 830 mV (vs. Ag/AgCl). Selectivity for ascorbate and dopamine as well as detection limit for NO (1.5 nM at S/N=3) is 5-10 times better than parameters usually reported for Nafion coated porphyrinic sensors. Nafion coating can further enhance selectivity properties as well as aids to the stability of the sensors' responses.

Citace poskytuje Crossref.org

Najít záznam

Citační ukazatele

Nahrávání dat ...

    Možnosti archivace