Silicon nanocrystals (SiNCs) smaller than 5 nm are a material with strong visible photoluminescence (PL). However, the physical origin of the PL, which, in the case of oxide-passivated SiNCs, is typically composed of a slow-decaying red-orange band (S-band) and of a fast-decaying blue-green band (F-band), is still not fully understood. Here we present a physical interpretation of the F-band origin based on the results of an experimental study, in which we combine temperature (4-296 K), temporally (picosecond resolution) and spectrally resolved luminescence spectroscopy of free-standing oxide-passivated SiNCs. Our complex study shows that the F-band red-shifts only by 35 meV with increasing temperature, which is almost 6 times less than the red-shift of the S-band in a similar temperature range. In addition, the F-band characteristic decay time obtained from a stretched-exponential fit decreases only slightly with increasing temperature. These data strongly suggest that the F-band arises from the core-related quasi-direct radiative recombination governed by slowly thermalizing photoholes.

Institute of Physics Academy of Sciences of the Czech Republic v v i Cukrovarnická 10 162 53 Prague 6 Czech Republic

Citace poskytuje Crossref.org

Why do Si quantum dots with stronger fast emission have lower external photoluminescence quantum yield?

Silicon nanocrystal-based photonic crystal slabs with broadband and efficient directional light emission

Agglomeration of Luminescent Porous Silicon Nanoparticles in Colloidal Solutions