The binary system Sb-Se was studied via laser ablation using antimony-selenium mixtures made from powdered elements in various ratios generating new SbmSen clusters. The results show that in addition to Sbm+ (m = 1-8) and Sen+ (n = 2-9) clusters, a series of SbmSen+ clusters such as SbSe1-8+, Sb2Se1-6+, Sb3Se1-5+, Sb4Se1-3+, and Sb5Se1,2+ is generated. In addition, some low intensity oxidized clusters like Se6O2+, Se7O2+, and SbSe2-6O5+ and partially hydroxylated clusters (SbSeO2H7+, SbSe5O4H+) are also formed. In total, 24 new antimony selenide clusters were generated. The knowledge gained can contribute to the elucidation of the structure of SbmSen glasses. Graphical Abstract.

CEPLANT R and D Centre for Low Cost Plasma and Nanotechnology Surface Modification Masaryk University Kotlářská 2 61137 Brno Czech Republic

Department of Chemistry Faculty of Science Masaryk University Kamenice 5 A14 62500 Brno Czech Republic

Department of Physical Electronics Faculty of Science Masaryk University Kotlářská 2 61137 Brno Czech Republic

Zobrazit více v PubMed

Chemistry. 2011 Jun 6;17(24):6847-52 PubMed

Chemistry. 2016 Aug 1;22(32):11261-8 PubMed

Chem Sci. 2015 Sep 1;6(9):5255-5262 PubMed

Comparison of Clusters Produced from Sb2Se3 Homemade Polycrystalline Material, Thin Films, and Commercial Polycrystalline Bulk Using Laser Desorption Ionization with Time of Flight Quadrupole Ion Trap Mass Spectrometry

Mass spectrometric investigation of amorphous Ga-Sb-Se thin films