Three mechanically alloyed (MA) and spark plasma sintered (SPS) CoCrFeNiNbX (X = 5, 20, and 35 at.%) alloys with an addition of 5 at.% of SiC were investigated. The face-centered cubic (FCC) high-entropy solid solution, NbC carbides, and hexagonal Laves phase already developed during MA. In addition, the SPS compacting led to the formation of oxide particles in all alloys, and the Cr7C3 carbides in the Nb5 alloy. The fraction of the FCC solid solution decreased with increasing Nb concentration at the expense of the NbC carbide and the Laves phase. Long-term annealing at 800 °C led to the disappearance of the Cr7C3 carbide in the Nb5 alloy, and new oxides-Ni6Nb6O, Cr2O3, and CrNbO4-were formed. At laboratory temperature, the Nb5 alloy, containing only the FCC matrix and carbide particles, was relatively strong and very ductile. At a higher Nb content (Nb20 and Nb35), the alloys became brittle. After annealing for 100 h at 800 °C, the Nb5 alloy conserved its plasticity and the Nb20 and Nb35 alloys maintained or even increased their brittleness. When tested at 800 °C, the Nb5 and Nb20 alloys deformed almost identically (CYS ~450 MPa, UTS ~500 MPa, plasticity ~18%), whereas the Nb35 alloy was much stronger (CYS of 1695 MPa, UCS of 1817 MPa) and preserved comparable plasticity.

• Klíčová slova
• X-ray diffraction, compression testing, electron microscopy, high-entropy alloys, instrumented indentation, mechanical alloying, spark plasma sintering,
• Publikační typ
• časopisecké články MeSH

Powder metallurgy is a group of advanced processes for the synthesis, processing, and shaping of various kinds of materials. Initially inspired by ceramics processing, the methodology comprising of the production of a powder and its transformation to a compact solid product has attracted great attention since the end of World War II. At present, there are many technologies for powder production (e.g., gas atomization of the melt, chemical reduction, milling, and mechanical alloying) and its consolidation (e.g., pressing and sintering, hot isostatic pressing, and spark plasma sintering). The most promising ones can achieve an ultra-fine or nano-grained structure of the powder, and preserve it during consolidation. Among these methods, mechanical alloying and spark plasma sintering play a key role. This Special Issue gives special focus to the advancement of mechanical alloying, spark plasma sintering and self-propagating high-temperature synthesis methods, as well as to the role of these processes in the development of new materials.

• Klíčová slova
• mechanical alloying, powder metallurgy, self-propagating high-temperature synthesis, spark plasma sintering,
• Publikační typ
• úvodníky MeSH