The technique for fabrication of soft porous hydrogels, in which both the size and the orientation of inner pores can be controlled, was developed. Three-dimensional hydrophilic gels based on poly[2-hydroxyethyl methacrylate] are designed as scaffolds for regeneration of soft tissues, e.g., nerve tissue. Anisotropic macropores of the size ranging from 10 to 50 microm were formed (1) by using a porogen-leaching method with a solid organic porogen, (2) by phase-separation during gelation in solvent-nonsolvent mixture, or (3) by combination of solid porogen elimination and phase-separation. As a porogen, poly(L-lactide) fibers were applied and consequently washed away under mild conditions to obtain desired spatial orientation of pores. Highly water-swollen polymer gels were characterized with high pressure (low vacuum) scanning electron microscopy (AquaSEM). The morphology of voids remaining after removing the solid PLLA porogen (the macropores) was clearly shown.

Department of Bioanalogous and Special Polymers Institute of Macromolecular Chemistry Academy of Sciences of the Czech Republic Heyrovsky Sq 2 162 06 Prague 6 Czech Republic

Zobrazit více v PubMed

J Biomater Sci Polym Ed. 2005;16(12 ):1595-610 PubMed

Biomaterials. 2006 Jul;27(19):3515-8 PubMed

FASEB J. 1999 Dec;13(15):2214-24 PubMed

Nat Biotechnol. 2000 Apr;18(4):415-9 PubMed

Otolaryngol Head Neck Surg. 1990 Oct;103(4):509-18 PubMed

Science. 1982 May 21;216(4548):897-9 PubMed

J Neurobiol. 2005 Jan;62(1):134-47 PubMed

Biomaterials. 1988 Nov;9(6):494-9 PubMed

Exp Neurol. 1997 Feb;143(2):287-99 PubMed

Cell Transplant. 1993 May 1;2(3):229-239 PubMed

Biomaterials. 2000 Mar;21(5):529-36 PubMed

Microsurgery. 1998;18(4):270-5 PubMed

Enzymatic degradation of the hydrogels based on synthetic poly(α-amino acid)s