Photodynamic therapy (PDT) has garnered immense attention as a minimally invasive clinical treatment modality for malignant cancers. However, its low penetration depth and photodamage of living tissues by UV and visible light, which activate a photosensitizer, limit the application of PDT. In this study, monodisperse NaYF4 :Yb3+ /Er3+ nanospheres 20 nm in diameter, that serve as near-infrared (NIR)-to-visible light converters and activators of a photosensitizer, were synthesized by high-temperature co-precipitation of lanthanide chlorides in a high-boiling organic solvent (octadec-1-ene). The nanoparticles were coated with a thin shell (≈3 nm) of homogenous silica via the hydrolysis and condensation of tetramethyl orthosilicate. The NaYF4 :Yb3+ /Er3+ @SiO2 particles were further functionalized by methacrylate-terminated groups via 3-(trimethoxysilyl)propyl methacrylate. To introduce a large number of reactive amino groups on the particle surface, methacrylate-terminated NaYF4 :Yb3+ /Er3+ @SiO2 nanospheres were modified with a branched polyethyleneimine (PEI) via Michael addition. Aluminum carboxyphthalocyanine (Al Pc-COOH) was then conjugated to NaYF4 :Yb3+ /Er3+ @SiO2 -PEI nanospheres via carbodiimide chemistry. The resulting NaYF4 :Yb3+ /Er3+ @SiO2 -PEI-Pc particles were finally modified with succinimidyl ester of poly(ethylene glycol) (PEG) in order to alleviate their future uptake by the reticuloendothelial system. Upon 980 nm irradiation, the intensive red emission of NaYF4 :Yb3+ /Er3+ @SiO2 -PEI-Pc-PEG nanoparticles completely vanished, indicating efficient energy transfer from the nanoparticles to Al Pc-COOH, which generates singlet oxygen (1 O2 ). Last but not least, NaYF4 :Yb3+ /Er3+ @SiO2 -PEI-Pc-PEG nanospheres were intratumorally administered into mammary carcinoma MDA-MB-231 growing subcutaneously in athymic nude mice. Extensive necrosis developed at the tumor site of all mice 24-48 h after irradiation by laser at 980 nm wavelength. The results demonstrate that the NaYF4 :Yb3+ /Er3+ @SiO2 -PEI-Pc-PEG nanospheres have great potential as a novel NIR-triggered PDT nanoplatform for deep-tissue cancer therapy.

Department of Experimental Physics Wroclaw University of Science and Technology Wybrzeze Wyspianskiego 27 50 370 Wroclaw Poland

Institute of Biophysics and Informatics 1st Faculty of Medicine Charles University Salmovská 1 120 00 Prague 2 Czech Republic

Institute of Macromolecular Chemistry Academy of Sciences of the Czech Republic Heyrovského nám 2 162 06 Prague 6 Czech Republic

Citace poskytuje Crossref.org

Temoporfin-Conjugated PEGylated Poly(N,N-dimethylacrylamide)-Coated Upconversion Colloid for NIR-Induced Photodynamic Therapy of Pancreatic Cancer

Temoporfin-Conjugated Upconversion Nanoparticles for NIR-Induced Photodynamic Therapy: Studies with Pancreatic Adenocarcinoma Cells In Vitro and In Vivo

PEG-Neridronate-Modified NaYF4:Gd3+,Yb3+,Tm3+/NaGdF4 Core-Shell Upconverting Nanoparticles for Bimodal Magnetic Resonance/Optical Luminescence Imaging

Single-Nanocrystal Studies on the Homogeneity of the Optical Properties of NaYF4:Yb3+,Er3

Monodisperse Core-Shell NaYF4:Yb3+/Er3+@NaYF4:Nd3+-PEG-GGGRGDSGGGY-NH2 Nanoparticles Excitable at 808 and 980 nm: Design, Surface Engineering, and Application in Life Sciences

Magnetic Temperature-Sensitive Solid-Lipid Particles for Targeting and Killing Tumor Cells