Zinc (Zn) alloys seem to be promising candidates for application in orthopaedic or cardiovascular medical implants. In this area, high standards are required regarding the biocompatibility as well as excellent mechanical and tailored degradation properties. In the presented study, a novel Zn-0.8Mg-0.2Sr (wt%) alloy has been fabricated by the combination of casting, homogenization annealing and extrusion at 200 °C. As a consequence of its fine-grained homogenous microstructure, the prepared material is characterized by an excellent combination of tensile yield strength, ultimate tensile strength and elongation corresponding to 244 MPa, 324 MPa and 20% respectively. The in vitro corrosion rates of the Zn-0.8Mg-0.2Sr alloy in the physiological solution and the simulated body fluid were 244 μm/a and 69.8 μm/a, respectively. Furthermore, an extract test revealed that Zn-0.8Mg-0.2Sr extracts diluted to 25% had no adverse effects towards L929 fibroblasts, TAg periosteal cells and Saos-2 osteoblasts. Moreover, the Zn-0.8Mg-0.2Sr surface showed effective inhibition of initial Streptococcus gordonii adhesion and biofilm formation. These results indicated the Zn-0.8Mg-0.2Sr alloy, which has superior mechanical properties, might be a promising candidate for materials used for load-bearing applications.

FZU The Institute of Physics Czech Academy of Sciences Na Slovance 1999 2 Prague 8 182 21 Czech Republic

Institute of Metals and Corrosion Engineering University of Chemistry and Technology Technická 6 Prague 6 166 28 Czech Republic

Section Medical Materials Science and Technology University Hospital Tübingen Osianderstrasse 2 8 Tübingen 72076 Germany

Citace poskytuje Crossref.org

Zinc based biodegradable metals for bone repair and regeneration: Bioactivity and molecular mechanisms

Microstructural and Mechanical Characterization of Newly Developed Zn-Mg-CaO Composite

A Complex Evaluation of the In-Vivo Biocompatibility and Degradation of an Extruded ZnMgSr Absorbable Alloy Implanted into Rabbit Bones for 360 Days

Zn-0.8Mg-0.2Sr (wt.%) Absorbable Screws-An In-Vivo Biocompatibility and Degradation Pilot Study on a Rabbit Model