This study focuses on the experimental verification of residual stress (RS) in a 3D-printed braking pedal using the Powder Bed Fusion (PBF) method with SS316L material. The RS was measured at two representative locations using the hole drilling method (HDM) and the dividing method, which are semi-destructive and destructive methods of RS measurement, respectively. The finite element method (FEM) was used with Ansys Workbench 2020R2 and Simufact Additive 2021 software to determine the magnitude of RS. The results provide insights into how RS is incorporated into metal 3D-printed components and the available tools for predicting RS. This information is essential for experts to improve the accuracy and functionality of SLM parts when post-subtractive or additive manufacturing processes are used. Overall, this study contributes to the advancement of knowledge on the effects of RS on 3D-printed metal components, which can inform future research and development in this area.

• Klíčová slova
• SS316L, hole drilling method, powder bed fusion, residual stress,
• Publikační typ
• časopisecké články MeSH

Designing a composite, possibly strengthened by a dispersion of (fine) oxides, is a favorable way to improve the mechanical characteristics of Cu while maintaining its advantageous electric conductivity. The aim of this study was to perform mechanical alloying of a Cu powder with a powder of Al2O3 oxide, seal the powder mixture into evacuated Cu tubular containers, i.e., cans, and apply gradual direct consolidation via rotary swaging at elevated temperatures, as well as at room temperature (final passes) to find the most convenient way to produce the designed Al2O3 particle-strengthened Cu composite. The composites swaged with the total swaging degree of 1.83 to consolidated rods with a diameter of 10 mm were subjected to measurements of electroconductivity, investigations of mechanical behavior via compression testing, and detailed microstructure observations. The results revealed that the applied swaging degree was sufficient to fully consolidate the canned powders, even at moderate and ambient temperatures. In other words, the final structures, featuring ultra-fine grains, did not exhibit voids or remnants of unconsolidated powder particles. The swaged composites featured favorable plasticity regardless of the selected processing route. The flow stress curves exhibited the establishment of steady states with increasing strain, regardless of the applied strain rate. The electroconductivity of the composite swaged at elevated temperatures, featuring homogeneous distribution of strengthening oxide particles and the average grain size of 1.8 µm2, reaching 80% IACS (International Annealed Copper Standard).

• Klíčová slova
• composite, copper, microstructure, oxide dispersion, rotary swaging,
• Publikační typ
• časopisecké články MeSH