Mortars and concretes are ubiquitous materials with very complex hierarchical microstructures. To fully understand their main properties and to decrease their CO2 footprint, a sound description of their spatially resolved mineralogy is necessary. Developing this knowledge is very challenging as about half of the volume of hydrated cement is a nanocrystalline component, calcium silicate hydrate (C-S-H) gel. Furthermore, other poorly crystalline phases (e.g. iron siliceous hydrogarnet or silica oxide) may coexist, which are even more difficult to characterize. Traditional spatially resolved techniques such as electron microscopy involve complex sample preparation steps that often lead to artefacts (e.g. dehydration and microstructural changes). Here, synchrotron ptychographic tomography has been used to obtain spatially resolved information on three unaltered representative samples: neat Portland paste, Portland-calcite and Portland-fly-ash blend pastes with a spatial resolution below 100 nm in samples with a volume of up to 5 × 104 µm3. For the neat Portland paste, the ptychotomographic study gave densities of 2.11 and 2.52 g cm-3 and a content of 41.1 and 6.4 vol% for nanocrystalline C-S-H gel and poorly crystalline iron siliceous hydrogarnet, respectively. Furthermore, the spatially resolved volumetric mass-density information has allowed characterization of inner-product and outer-product C-S-H gels. The average density of the inner-product C-S-H is smaller than that of the outer product and its variability is larger. Full characterization of the pastes, including segmentation of the different components, is reported and the contents are compared with the results obtained by thermodynamic modelling.

ALBA Synchrotron Carrer de la Llum 2 26 E 08290 Cerdanyola del Vallès Barcelona Spain

Departamento de Química Inorgánica Cristalografía y Mineralogía Universidad de Málaga 29071 Malaga Spain

EMPA Laboratory for Concrete and Construction Chemistry Überlandstrasse 129 CH 8600 Dübendorf Switzerland

Faculty of Civil Engineering Czech Technical University Prague 166 29 Prague Czech Republic

Paul Scherrer Institut 5232 Villigen PSI Switzerland

See more in PubMed

Abràmoff, M. D., Magalhães, P. J. & Ram, S. J. (2004). Biophotonics Int. 11, 36–42.

Allen, A. J., Thomas, J. J. & Jennings, H. M. (2007). Nat. Mater. 6, 311–316. PubMed

Andalibi, M. R., Kumar, A., Srinivasan, B., Bowen, P., Scrivener, K., Ludwig, C. & Testino, A. (2018). J. Mater. Chem. A, 6, 363–373.

Aranda, M. A. G. (2016). Crystallogr. Rev. 22, 150–196.

Artioli, G., Cerulli, T., Cruciani, G., Dalconi, M. C., Ferrari, G., Parisatto, M., Rack, A. & Tucoulou, R. (2010). Anal. Bioanal. Chem. 397, 2131–2136. PubMed

Artioli, G., Valentini, L., Voltolini, M., Dalconi, M. C., Ferrari, G. & Russo, V. (2015). Cryst. Growth Des. 15, 20–23.

Bae, S., Taylor, R., Shapiro, D., Denes, P., Joseph, J., Celestre, R., Marchesini, S., Padmore, H., Tyliszczak, T., Warwick, T., Kilcoyne, D., Levitz, P. & M Monteiro, P. J. (2015). J. Am. Ceram. Soc. 98, 4090–4095.

Baquerizo, L. G., Matschei, T., Scrivener, K. L., Saeidpour, M. & Wadsö, L. (2015). Cem. Concr. Res. 73, 143–157.

Barcelo, L., Kline, J., Walenta, G. & Gartner, E. (2014). Mater. Struct. 47, 1055–1065.

Bensted, J. & Barnes, P. (2002). Structure and Performance of Cements, 2nd ed. London: Spon Press.

Bentz, D. P., Quenard, D. A., Kunzel, H. M., Baruchel, J., Peyrin, F., Martys, N. S. & Garboczi, E. J. (2000). Mater. Struct. 33, 147–153.

Birkbak, M. E., Leemreize, H., Frølich, S., Stock, S. R. & Birkedal, H. (2015). Nanoscale. 7, 18402–18410. PubMed PMC

Chatterton, P. A. & Cross, J. D. (1972). Nat. Phys. Sci. 236, 91–92.

Chen, J. J., Sorelli, L., Vandamme, M., Ulm, F.-J. & Chanvillard, G. (2010). J. Am. Ceram. Soc. 93, 1484–1493.

Claret, F., Grangeon, S., Loschetter, A., Tournassat, C., De Nolf, W., Harker, N., Boulahya, F., Gaboreau, S., Linard, Y., Bourbon, X., Fernandez-Martinez, A. & Wright, J. (2018). IUCrJ, 5, 150–157. PubMed PMC

Cong, X. & Kirkpatrick, R. J. (1996). J. Am. Ceram. Soc. 79, 1585–1592.

Cuesta, A., De la Torre, A. G., Santacruz, I., Trtik, P., da Silva, J. C., Diaz, A., Holler, M. & Aranda, M. A. G. (2017a). J. Phys. Chem. C, 121, 3044–3054.

Cuesta, A., De la Torre, A. G., Santacruz, I., Trtik, P., da Silva, J. C., Diaz, A., Holler, M. & Aranda, M. A. G. (2017b). 39th International Conference on Cement Microscopy (ICMA 2017), 9–13 April 2017, Toronto, Ontario, Canada, pp. 17–32.

Cuesta, A., Zea-Garcia, J. D., Londono-Zuluaga, D., De la Torre, A. G., Santacruz, I., Vallcorba, O. & Aranda, M. A. G. (2017). Crystals, 7, 317. PubMed PMC

Cuesta, A., Zea-Garcia, J. D., Londono-Zuluaga, D., De la Torre, A. G., Santacruz, I., Vallcorba, O., Dapiaggi, M., Sanfélix, S. G. & Aranda, M. A. G. (2018). Sci. Rep. 8, 8544. PubMed PMC

Cullity, B. D. (1956). J. Chem. Educ. , 34, A178.

Deboodt, T., Ideker, J. H., Isgor, O. B. & Wildenschild, D. (2017). Constr. Build. Mater. 157, 476–488.

Deschner, F., Winnefeld, F., Lothenbach, B., Seufert, S., Schwesig, P., Dittrich, S., Goetz-Neunhoeffer, F. & Neubauer, J. (2012). Cem. Concr. Res. 42, 1389–1400.

De Weerdt, K., Haha, M., Le Saout, G., Kjellsen, K. O., Justnes, H. & Lothenbach, B. (2011). Cem. Concr. Res. 41, 279–291.

Diamond, S. (2004). Cem. Concr. Compos. 26, 919–933.

Diaz, A., Trtik, P., Guizar-Sicairos, M., Menzel, A., Thibault, P. & Bunk, O. (2012). Phys. Rev. B, 85, 020104.

Dierolf, M., Menzel, A., Thibault, P., Schneider, P., Kewish, C. M., Wepf, R., Bunk, O. & Pfeiffer, F. (2010). Nature, 467, 436–439. PubMed

Dilnesa, B. Z., Lothenbach, B., Renaudin, G., Wichser, A. & Kulik, D. (2014). Cem. Concr. Res. 59, 96–111.

Dilnesa, B. Z., Wieland, E., Lothenbach, B., Dähn, R. & Scrivener, K. L. (2014). Cem. Concr. Res. 58, 45–55.

Dinapoli, R., Bergamaschi, A., Henrich, B., Horisberger, R., Johnson, I., Mozzanica, A., Schmid, E., Schmitt, B., Schreiber, A., Shi, X. & Theidel, G. (2011). Nucl. Instrum. Methods, 650, 79–83.

Edo, T. B., Batey, D. J., Maiden, A. M., Rau, C., Wagner, U., Pešić, Z. D., Waigh, T. A. & Rodenburg, J. M. (2013). Phys. Rev. A, 87, 053850.

Faulkner, H. M. L. & Rodenburg, J. M. (2004). Phys. Rev. Lett. 93, 023903. PubMed

Gallucci, E., Scrivener, K., Groso, A., Stampanoni, M. & Margaritondo, G. (2007). Cem. Concr. Res. 37, 360–368.

García-Materé, M., De la Torre, A. G. G., León-Reina, L., Aranda, M. A. G. A. G. & Santacruz, I. (2013). Cem. Concr. Res. 54, 12–20.

Gastaldi, D., Canonico, F., Capelli, L., Boccaleri, E., Milanesio, M., Palin, L., Croce, G., Marone, F., Mader, K. & Stampanoni, M. (2012). Constr. Build. Mater. 29, 284–290.

Geng, G., Li, J., Yu, Y.-S., Shapiro, D. A., Kilcoyne, D. A. L. & Monteiro, P. J. M. (2017). Cryst. Growth Des. 17, 4246–4253.

Geng, G., Myers, R. J., Li, J., Maboudian, R., Carraro, C., Shapiro, D. A. & Monteiro, P. J. M. (2017). Sci. Rep. 7, 44032. PubMed PMC

Geng, G., Myers, R. J., Yu, Y.-S., Shapiro, D. A., Winarski, R., Levitz, P. E., Kilcoyne, D. A. L. & Monteiro, P. J. M. (2018). Cem. Concr. Res. 111, 130–137.

Gorelick, S., Vila-Comamala, J., Guzenko, V. A., Barrett, R., Salomé, M. & David, C. (2011). J. Synchrotron Radiat. 18, 442–446. PubMed PMC

Grangeon, S., Fernandez-Martinez, A., Baronnet, A., Marty, N., Poulain, A., Elkaïm, E., Roosz, C., Gaboreau, S., Henocq, P. & Claret, F. (2017). J. Appl. Cryst. 50, 14–21. PubMed PMC

Guizar-Sicairos, M., Boon, J. J., Mader, K., Diaz, A., Menzel, A. & Bunk, O. (2015). Optica. 2, 259.

Guizar-Sicairos, M., Diaz, A., Holler, M., Lucas, M. S., Menzel, A., Wepf, R. A. & Bunk, O. (2011). Opt. Express, 19, 21345–21357. PubMed

Guizar-Sicairos, M. & Fienup, J. R. (2008). Opt. Express, 16, 7264–7278. PubMed

Hanehara, S., Tomosawa, F., Kobayakawa, M. & Hwang, K. R. (2001). Cem. Concr. Res. 31, 31–39.

Heel, M. van & Schatz, M. (2005). J. Struct. Biol. 151, 250–262. PubMed

Henke, B. L., Gullikson, E. M. & Davis, J. C. (1993). At. Data Nucl. Data Tables, 54, 181–342.

Hernández-Cruz, D., Hargis, C. W., Dominowski, J., Radler, M. J. & Monteiro, P. J. M. (2016). Cem. Concr. Compos. 68, 123–130.

Holler, M., Diaz, A., Guizar-Sicairos, M., Karvinen, P., Färm, E., Härkönen, E., Ritala, M., Menzel, A., Raabe, J. & Bunk, O. (2014). Sci. Rep. 4, 3857. PubMed PMC

Holler, M., Guizar-Sicairos, M., Tsai, E. H. R., Dinapoli, R., Müller, E., Bunk, O., Raabe, J. & Aeppli, G. (2017). Nature, 543, 402–406. PubMed

Holler, M. & Raabe, J. (2015). Opt. Eng. 54, 054101.

Holler, M., Raabe, J., Diaz, A., Quitmann, C., Menzel, A. & Bunk, O. (2012). Rev. Sci. Instrum. 83, 073703. PubMed

Howells, M. R., Beetz, T., Chapman, H. N., Cui, C., Holton, J. M., Kirz, J., Lima, E., Marchesini, S., Miao, H., Sayre, D., Shapiro, D. A., Spence, J. C. H. & Starodub, D. (2009). J. Electron Spectros. Relat. Phenomena. 170, 4–12. PubMed PMC

Huang, X., Yan, H., Harder, R., Hwu, Y., Robinson, I. K. & Chu, Y. S. (2014). Opt. Express. 22, 12634. PubMed

Jennings, H. M. (2008). Cem. Concr. Res. 38, 275–289.

Juenger, M. C. G. & Siddique, R. (2015). Cem. Concr. Res. 78, 71–80.

Kaestner, A., Munch, B., Trtik, P. & Butler, L. (2011). Opt. Eng. 50, 123201.

Kosmatka, S. H., Kerkhoff, B. & Panarese, W. C. (1996). Des. Control Concr. Mix. pp. 57–72.

Kulik, D. A., Wagner, T., Dmytrieva, S. V., Kosakowski, G., Hingerl, F. F., Chudnenko, K. V. & Berner, U. R. (2013). Comput. Geosci. 17, 1–24.

Kumar, A., Walder, B. J., Kunhi Mohamed, A., Hofstetter, A., Srinivasan, B., Rossini, A. J., Scrivener, K., Emsley, L. & Bowen, P. (2017). J. Phys. Chem. C, 121, 17188–17196.

Liu, Y. & Daum, P. H. (2008). J. Aerosol Sci. 39, 974–986

Lothenbach, B., Kulik, D. A., Matschei, T., Balonis, M., Baquerizo, L., Dilnesa, B., Miron, G. D. & Myers, R. J. (2019). Cem. Concr. Res. 115, 472–506.

Lothenbach, B., Le Saout, G., Gallucci, E. & Scrivener, K. (2008). Cem. Concr. Res. 38, 848–860.

Lothenbach, B., Scrivener, K. & Hooton, R. D. (2011). Cem. Concr. Res. 41, 1244–1256.

Ludwig, H.-M. & Zhang, W. (2015). Cem. Concr. Res. 78, 24–37.

Marinoni, N., Voltolini, M., Mancini, L. & Cella, F. (2012). J. Mater. Sci. 47, 2845–2855.

Matschei, T., Lothenbach, B. & Glasser, F. P. (2007a). Cem. Concr. Res. 37, 118–130.

Matschei, T., Lothenbach, B. & Glasser, F. P. (2007b). Cem. Concr. Res. 37, 551–558.

Mehta, P. K. & Monteiro, P. J. M. (2014). Concrete: Microstructure, Properties, and Materials, 4th ed. New York: McGraw-Hill Education.

Moradian, M., Hu, Q., Aboustait, M., Ley, M. T., Hanan, J. C., Xiao, X., Scherer, G. W. & Zhang, Z. (2017). Mater. Des. 136, 137–149.

Muller, A. C. A., Scrivener, K. L., Gajewicz, A. M. & McDonald, P. J. (2013). J. Phys. Chem. C, 117, 403–412.

Ouzia, A. & Scrivener, K. (2019). Cem. Concr. Res. 115, 339–360.

Pacewska, B. & Wilińska, I. (2013). Procedia Eng. 57, 53–62.

Palkovic, S. D., Brommer, D. B., Kupwade-Patil, K., Masic, A., Buehler, M. J. & Büyüköztürk, O. (2016). Constr. Build. Mater. 115, 13–31.

Papadakis, V. G. (1999). Cem. Concr. Res. 29, 1727–1736.

Papatzani, S., Paine, K. & Calabria-Holley, J. (2015). Constr. Build. Mater. 74, 219–234.

Parisatto, M., Dalconi, M. C., Valentini, L., Artioli, G., Rack, A., Tucoulou, R., Cruciani, G. & Ferrari, G. (2015). J. Mater. Sci. 50, 1805–1817.

Pöllmann, H. (2017). Cementitious Materials: Composition, Properties, Application. Berlin, Boston: De Gruyter.

Promentilla, M., Cortez, S., Papel, R., Tablada, B., Sugiyama, T., Promentilla, M. A. B., Cortez, S. M., Papel, R. A. D., Tablada, B. M. & Sugiyama, T. (2016). Materials (Basel), 9, 388.

Promentilla, M. A. B., Sugiyama, T., Hitomi, T. & Takeda, N. (2009). Cem. Concr. Res. 39, 548–557.

Richardson, I. G. (2008). Cem. Concr. Res. 38, 137–158.

Richardson, I. G. (2014). Acta Cryst. B70, 903–923. PubMed PMC

Rodenburg, J. M., Hurst, A. C., Cullis, A. G., Dobson, B. R., Pfeiffer, F., Bunk, O., David, C., Jefimovs, K. & Johnson, I. (2007). Phys. Rev. Lett. 98, 034801. PubMed

Roosz, C., Gaboreau, S., Grangeon, S., Prêt, D., Montouillout, V., Maubec, N., Ory, S., Blanc, P., Vieillard, P. & Henocq, P. (2016). Langmuir, 32, 6794–6805. PubMed

Sánchez-Herrero, M. J., Fernández-Jiménez, A. & Palomo, Á. (2016). J. Am. Ceram. Soc. 99, 604–611.

Schindelin, J., Arganda-Carreras, I., Frise, E., Kaynig, V., Longair, M., Pietzsch, T., Preibisch, S., Rueden, C., Saalfeld, S., Schmid, B., Tinevez, J.-Y., White, D. J., Hartenstein, V., Eliceiri, K., Tomancak, P. & Cardona, A. (2012). Nat. Methods, 9, 676–682. PubMed PMC

Scrivener, K., Snellings, R. & Lothenbach, B. (2016). A Practical Guide to Microstructural Analysis of Cementitious Materials. Boca Raton: CRC Press.

Scrivener, K. L., Lothenbach, B., De Belie, N., Gruyaert, E., Skibsted, J., Snellings, R. & Vollpracht, A. (2015). Mater. Struct. 48, 835–862.

Shahmoradian, S. H., Tsai, E. H. R., Diaz, A., Guizar-Sicairos, M., Raabe, J., Spycher, L., Britschgi, M., Ruf, A., Stahlberg, H. & Holler, M. (2017). Sci. Rep. 7, 6291. PubMed PMC

Silva, J. C. da & Menzel, A. (2015). Opt. Express, 23, 33812–33821. PubMed

Silva, J. C. da, Trtik, P., Diaz, A., Holler, M., Guizar-Sicairos, M., Raabe, J., Bunk, O. & Menzel, A. (2015). Langmuir, 31, 3779–3783. PubMed

Skinner, L. B., Chae, S. R., Benmore, C. J., Wenk, H. R. & Monteiro, P. J. M. (2010). Phys. Rev. Lett. 104, 195502. PubMed

S˘milauer, V. & Bittnar, Z. (2006). Cem. Concr. Res. 36, 1708–1718.

Soin, A. V., Catalan, L. J. J. & Kinrade, S. D. (2013). Cem. Concr. Res. 48, 17–24.

Stitt, C. A., Paraskevoulakos, C., Banos, A., Harker, N. J., Hallam, K. R., Davenport, A., Street, S. & Scott, T. B. (2017). Sci. Rep. 7, 7999. PubMed PMC

Stitt, C. A., Paraskevoulakos, C., Banos, A., Harker, N. J., Hallam, K. R., Pullin, H., Davenport, A., Street, S. & Scott, T. B. (2018). Sci. Rep. 8, 9282. PubMed PMC

Sugiyama, T., Promentilla, M. A. B., Hitomi, T. & Takeda, N. (2010). Cem. Concr. Res. 40, 1265–1270.

Taylor, H. F. W. (1997). Cement Chemistry. London: Academic Press.

Thibault, P., Dierolf, M., Bunk, O., Menzel, A. & Pfeiffer, F. (2009). Ultramicroscopy, 109, 338–343. PubMed

Thibault, P. & Guizar-Sicairos, M. (2012). New J. Phys. 14, 063004.

Thomas, J. J., Jennings, H. M. & Allen, A. J. (2010). J. Phys. Chem. C, 114, 7594–7601.

Trtik, P., Diaz, A., Guizar-Sicairos, M., Menzel, A. & Bunk, O. (2013). Cem. Concr. Compos. 36, 71–77.

Trtik, P., Kaufmann, J. & Volz, U. (2012). Cem. Concr. Res. 42, 215–221.

Tsai, E. H. R., Usov, I., Diaz, A., Menzel, A. & Guizar-Sicairos, M. (2016). Opt. Express, 24, 29089. PubMed

Valentini, L., Artioli, G., Voltolini, M. & Dalconi, M. C. (2012). J. Am. Ceram. Soc. 95, 2647–2652.

Valentini, L., Dalconi, M. C., Parisatto, M., Cruciani, G. & Artioli, G. (2011). J. Appl. Cryst. 44, 272–280.

Vespa, M., Wieland, E., Dähn, R. & Lothenbach, B. (2015). J. Am. Ceram. Soc. 98, 2286–2294.

Voltolini, M., Dalconi, M. C., Artioli, G., Parisatto, M., Valentini, L., Russo, V., Bonnin, A. & Tucoulou, R. (2013). J. Appl. Cryst. 46, 142–152.

Voltolini, M., Marinoni, N. & Mancini, L. (2011). J. Mater. Sci. 46, 6633–6641.

Wagner, T., Kulik, D. A., Hingerl, F. F. & Dmytrieva, S. V. (2012). Can. Mineral. 50, 1173–1195.

Yang, F., Griffa, M., Bonnin, A., Mokso, R., Di Bella, C., Münch, B., Kaufmann, R. & Lura, P. (2016). J. Microsc. 261, 88–104. PubMed

Zhang, M. (2017). Cem. Concr. Res. 95, 18–29.