Modern tissue engineering requires not only degradable materials promoting cell growth and differentiation, but also vascularization of the engineered tissue. Porous polylactide/polycaprolactone (PLA/PCL, ratio 3/5) foam scaffolds were prepared by a combined porogen leaching and freeze-drying technique using NaCl (crystal size 250-500 µm) and a water-soluble cellulose derivative (KlucelTM E; 10-100% w/w relative to the total PLA/PCL concentration) as porogens. Scanning electron microscopy, micro-CT, and Brunauer-Emmett-Teller analysis showed that all scaffolds contained a trimodal range of pore sizes, i.e., macropores (average diameter 298-539 μm), micropores (100 nm to 10 μm), and nanopores (mostly around 3.0 nm). All scaffolds had an open porosity of about 90%, and the pores were interconnected. The size of the macropores and the nanoporosity were higher in the scaffolds prepared with Klucel. Nanoporosity increased water uptake by the scaffolds, while macroporosity promoted cell ingrowth, which was most evident in scaffolds prepared with 25% Klucel. Human adipose-derived stem cells co-cultured with endothelial cells formed pre-vascular structures in the scaffolds, which was further enhanced in a dynamic cell culture system. The scaffolds are promising for the engineering of pre-vascularized soft tissues (relatively pliable 10% Klucel scaffolds) and hard tissues (mechanically stronger 25% and 50% Klucel scaffolds).

• Klíčová slova
• compression stress and strain, degradable polyesters, dynamic cultivation, endothelial cells, macroporosity, mesenchymal stem cells, mineralization, nanoporosity, pre-vascularization, three-dimensional scaffolds,
• MeSH
• biokompatibilní materiály chemie   MeSH
• kmenové buňky cytologie   MeSH
• lidé MeSH
• polyestery * chemie   MeSH
• poréznost MeSH
• tkáňové inženýrství * metody   MeSH
• tkáňové podpůrné struktury * chemie   MeSH
• tuková tkáň cytologie   MeSH
• Check Tag
• lidé MeSH
• Publikační typ
• časopisecké články MeSH
• Názvy látek
• biokompatibilní materiály MeSH
• poly(lactide) MeSH Prohlížeč
• polycaprolactone MeSH Prohlížeč
• polyestery * MeSH

We compared the applicability of 3D fibrous scaffolds, produced by our patented centrifugal spinning technology, in soft tissue engineering. The scaffolds were prepared from four different biocompatible and biodegradable thermoplastics, namely, polylactide (PLA), polycaprolactone (PCL), poly(3-hydroxybutyrate) (PHB), and poly(1,4-butylene succinate) (PBS) and their blends. The combined results of SEM and BET analyses revealed an internal hierarchically organized porosity of the polymeric micro/nanofibers. Both nanoporosity and capillary effect are crucial for the water retention capacity of scaffolds designed for tissue engineering. The increased surface area provided by nanoporosity enhances water retention, while the capillary effect facilitates the movement of water and nutrients within the scaffolds. When the scaffolds were seeded with adipose-derived stem cells (ASCs), the ingrowth of these cells was the deepest in the PLA/PCL 13.5/4 (w/w) composite scaffolds. This result is consistent with the relatively large pore size in the fibrous networks, the high internal porosity, and the large specific surface area found in these scaffolds, which may therefore be best suited as a component of adipose tissue substitutes that could reduce postoperative tissue atrophy. Adipose tissue constructs produced in this way could be used in the future instead of conventional fat grafts, for example, in breast reconstruction following cancer ablation.

• Klíčová slova
• PBS, PCL, PHB, PLA, bioartificial adipose tissue, centrifugal spinning technology, hierarchical inner porosity of fibers, mesenchymal stem cells, micro/nanofibrous scaffolds, tissue engineering,
• Publikační typ
• časopisecké články MeSH

Here, we report on the nanopatterning of different aromatic polymer substrates achieved by KrF excimer laser treatment. The conditions for the construction of the laser-induced periodic surface structures, the so-called LIPSS pattern, were established by optimized laser fluence and a number of pulses. The polymer substrates were polyethylene naphthalate (PEN), polyethersulfone (PES), and polystyrene (PS), which were chosen since they are thermally, chemically, and mechanically resistant polymers with high absorption coefficients at the excimer laser wavelength. The surface morphology of the treated substrates was investigated by atomic force microscopy and scanning electron microscopy, and the roughness and effective surface area on the modified samples were determined. Elemental concentration was characterized by energy-dispersive (EDX) analysis, surface chemistry was determined with X-ray photoelectron spectroscopy (XPS). The samples with the formation of LIPSS induced by 10 mJ·cm-2 with 1000, 3000, and 6000 pulses were used for subsequent in vitro cytocompatibility tests using human cells from osteosarcoma (U-2 OS). The LIPSS pattern and its ability of significant cell guidance were confirmed for some of the studied samples. Cell morphology, adhesion, and proliferation were evaluated. The results strongly contribute to the development of novel applications using nanopatterned polymers, e.g., in tissue engineering, cell analysis or in combination with metallization for sensor construction.

• Klíčová slova
• LIPSS, cell guidance, cytocompatibility, elemental analysis, excimer laser, human cells, periodic pattern, polymer,
• MeSH
• lasery MeSH
• lidé MeSH
• mezibuněčná komunikace MeSH
• nanostruktury * chemie   MeSH
• polymery chemie   MeSH
• povrchové vlastnosti MeSH
• savci MeSH
• zvířata MeSH
• Check Tag
• lidé MeSH
• zvířata MeSH
• Publikační typ
• časopisecké články MeSH
• Názvy látek
• polymery MeSH