In this work, a hybrid copolymer consisting of poly(3-hydroxybutyrate) grafted to hyaluronic acid (HA) was synthesised and characterised. Once formed, the P(3HB)-g-HA copolymer was soluble in water allowing a green electrospinning process. The diameters of nanofibres can be tailored by simply varying the Mw of polymer. The optimization of the process allowed to produce fibres of average diameter in the range of 100-150 nm and low polydispersity. The hydrophobic modification has not only increased the fibre diameter, but also the obtained layers were homogenous. At the nanoscale, the hybrid copolymer exhibited an unusual hairy topography. Moreover, the hardness and tensile properties of the hybrid were found to be superior compared to fibres made of unmodified HA. Particularly, this reinforcement was achieved at the longitudinal direction. Additionally, this work reports the use in the composition of a water-soluble copolymer containing photo cross-linkable moieties to produce insoluble materials post-electrospinning. The derivatives as well as their nanofibrous mats retain the biocompatibility of the natural polymers used for the fabrication.

Contipro a s Dolní Dobrouč 401 Dolní Dobrouč 561 02 Czech Republic

Department of General and Inorganic Chemistry Faculty of Chemical Technology University of Pardubice Studentská 573 Pardubice 532 10 Czech Republic

Department of Life Science Faculty of Science and Technology University of Westminster 115 New Cavendish Street London W1W 6UW UK

See more in PubMed

J Biomater Sci Polym Ed. 2014;25(4):370-93 PubMed

Int J Pharm. 2013 Oct 15;455(1-2):338-47 PubMed

Acta Biomater. 2015 Apr;16:23-34 PubMed

J Biomed Mater Res A. 2008 Jun 15;85(4):1072-81 PubMed

Carbohydr Polym. 2016 Feb 10;137:255-263 PubMed

Mater Sci Eng C Mater Biol Appl. 2017 Jan 1;70(Pt 2):1107-1119 PubMed

J Mater Sci Mater Med. 2016 Nov;27(11):165 PubMed

Int J Biol Macromol. 2018 Jan;106:692-697 PubMed

Carbohydr Polym. 2017 Sep 1;171:220-228 PubMed

Biotechnol Adv. 2017 Mar - Apr;35(2):240-250 PubMed

Int J Biol Macromol. 2016 Mar;84:174-81 PubMed

Biomaterials. 2003 Nov;24(25):4621-9 PubMed

J Funct Biomater. 2017 Feb 13;8(1): PubMed

Biomed Pharmacother. 2017 Feb;86:143-148 PubMed

Mater Sci Eng C Mater Biol Appl. 2013 May 1;33(4):1963-8 PubMed

Tissue Eng Part B Rev. 2013 Dec;19(6):485-502 PubMed

Bioact Mater. 2016 Jul 26;1(1):56-64 PubMed

Materials (Basel). 2017 Aug 29;10(9):null PubMed

Saudi J Biol Sci. 2018 Mar;25(3):545-550 PubMed