The aim of the present paper was to examine the irradiation effect of two doses of UVA rays (365 nm) on the rabbit cornea and lens. Corneas of anesthetized adult albino rabbits were irradiated with UVA rays for 5 days (daily dose 1.01 J cm(-2) in one group of rabbits and daily dose 2.02 J cm(-2) in the second group of animals). The third day after the last irradiation, the rabbits were killed, and their eyes were employed for spectrophotometrical, biochemical and immunohistochemical investigations. Normal eyes served as controls. Absorption spectra of the whole corneal centers were recorded over the UV-VIS (visible) spectral range. Levels of antioxidant and prooxidant enzymes, nitric oxide synthases and nitric oxide (indirectly measured as nitrate concentration) were investigated in the cornea. Malondialdehyde, a byproduct of lipid peroxidation, was examined in the cornea and lens. The results show that the staining for endothelial nitric oxide synthase was more pronounced in corneas irradiated with the higher UVA dose. Otherwise, UVA rays at either dose did not significantly change corneal light absorption properties and did not cause statistically significant metabolic changes in the cornea or lens. In conclusion, UVA rays at the employed doses did not evoke harmful effects in the cornea or lens.
The present study is bringing a comparison of surface morphology for various types of contact lenses. A novel method--scanning electron microscopy under aqueous conditions (cryo-SEM)--was tested for visualization of lenses at magnifications up to 2000x. For imaging lens surface on nanometre scale, we employed atomic force microscopy (AFM) in aqueous media. Various materials of lenses, based on silicone hydrogels or conventional hydrogels, were investigated. Total, 10 types of contact lenses from five manufacturers were selected and probed. We found that different methods of lens manufacture (lathe-cutting, cast-moulding, and spin casting) led to different values of surface roughness. In the swollen state, roughness values of lens surfaces lie between 4 and 140 nm. Lenses manufactured by lathe-cutting exhibit notable higher values, so that they could be easily distinguished from others. In cast-moulded lenses, the surface roughness decreased with increasing water content. Moreover, additional treatments of lenses introduced unique structural motifs onto surface. For instance, porous structure was found on lens surface finalized with plasma oxidation.
- MeSH
- biomedicínské technologie MeSH
- financování organizované MeSH
- hydrogely MeSH
- kontaktní čočky MeSH
- lidé MeSH
- mikroskopie atomárních sil metody MeSH
- mikroskopie elektronová rastrovací metody MeSH
- nanotechnologie MeSH
- povrchové vlastnosti MeSH
- roztoky MeSH
- silikony MeSH
- zmrazování MeSH
- Check Tag
- lidé MeSH
Under normal conditions, the cornea absorbs the majority of UVB (ultraviolet B, 280-320 nm) rays, which is very important for the protection of the inner eye against their damaging effect. Our previous studies have shown that repeated irradiation of the rabbit cornea with UVB rays for 5 days (daily dose of 1.01 J cm(- 2)) caused photokeratitis accompanied by swelling (hydration) of the corneal stroma, thinning of the corneal epithelium and decrease in antioxidants. The purpose of this study was to examine the light absorption properties of such damaged rabbit cornea. Results of both spectrophotometry of the whole corneal buttons and corneal tissue dissolved in sodium hydroxide show that because of above mentioned disturbances, UVB-irradiated cornea absorbs more light throughout the whole measurable UV-VIS spectral range than the normal cornea. Increased corneal thickness (result of hydration), changes of corneal transparency (the cornea becomes grayish) and some increase in protein content all contribute to the increased light absorption of UVB irradiated corneas. We suggest that the UVB-irradiated cornea, although damaged and nearly without antioxidants, might actually through its higher UV absorbance protect the inner eye against further damage from UVB rays.