OBJECTIVE: Dental hypersensitivity remains widespread, underscoring the need for materials that can effectively seal dental tubules. This study evaluated the potential of bioactive-glass-infused hydroxyethyl cellulose gels in this context. METHODS: Five gels were synthesized, each containing 20% bioactive glass (specifically, 45S5, S53P4, Biomin F, and Biomin C), with an additional blank gel serving as a control. Subjected to two months of accelerated aging at 37 ± 2 °C, these gels were assessed for key properties: viscosity, water disintegration time, pH level, consistency, adhesion to glass, and element release capability. RESULTS: Across the board, the gels facilitated the release of calcium, phosphate, and silicon ions, raising the pH from 9.00 ± 0.10 to 9.7 ± 0.0-a range conducive to remineralization. Dissolution in water occurred within 30-50 min post-application. Viscosity readings showed variability, with 45S5 reaching 6337 ± 24 mPa/s and Biomin F at 3269 ± 18 mPa/s after two months. Initial adhesion for the blank gel was measured at 0.27 ± 0.04 Pa, increasing to 0.73 ± 0.06 Pa for the others over time. Gels can release elements upon contact with water (Ca- Biomin C 104.8 ± 15.7 mg/L; Na- Biomin F 76.30 ± 11.44 mg/L; P- Biomin C 2.623 ± 0.393 mg/L; Si- 45S5-45.15 ± 6.77mg/L, F- Biomin F- 3.256 ± 0.651mg/L; Cl- Biomin C 135.5 ± 20.3 mg/L after 45 min). CONCLUSIONS: These findings highlight the gels' capacity to kickstart the remineralization process by delivering critical ions needed for enamel layer reconstruction. Further exploration in more dynamic, real-world conditions is recommended to fully ascertain their practical utility.
- Publikační typ
- časopisecké články MeSH
UNLABELLED: The aim of this study was to create a 3D printing material with bioactive properties that potentially could be used for a transparent removable orthodontic appliance. MATERIALS AND METHODS: To acrylic monomers, four bioactive glasses at 10% concentration were added, which release Ca, P, Si and F ions. The materials were printed on a 3D printer and tested for flexural strength (24 h and 30 days), sorption and solubility (7 days), ion release to artificial saliva pH = 4 and 7 (42 days) and cytotoxicity in the human fibroblast model. The released ions were determined by plasma spectrometry (Ca, P and Si ions) and ion-selective electrode (F measurement)s. RESULTS: The material obtained released Ca2+ and PO43- ions for a period of 42 days when using glass Biomin C at pH 4. The flexural strength depended on the direction in which the sample was printed relative to the 3D printer platform. Vertically printed samples had a resistance greater than 20%. The 10% Biomin C samples post-cured for 30 min with light had a survival rate of the cells after 72 h of 85%. CONCLUSIONS: Material for 3D printing with bioactive glass in its composition, which releases ions, can be used in the production of orthodontic aligners.
- Publikační typ
- časopisecké články MeSH
BACKGROUND: The creation of the denture base material with bioactive properties that releases ions and produces hydroxyapatite. METHODS: Acrylic resins were modified by the addition of 20% of four types of bioactive glasses by mixing with powders. Samples were subjected to flexural strength (1, 60 days), sorption and solubility (7 days), and ion release at pH 4 and pH 7 for 42 days. Hydroxyapatite layer formation was measured using infrared. RESULTS: Biomin F glass-containing samples release fluoride ions for a period of 42 days (pH = 4; Ca = 0.62 ± 0.09; P = 30.47 ± 4.35; Si = 22.9 ± 3.44; F = 3.1 ± 0.47 [mg/L]). The Biomin C (contained in the acrylic resin releases (pH = 4; Ca = 41.23 ± 6.19; P = 26.43 ± 3.96; Si = 33.63 ± 5.04 [mg/L]) ions for the same period of time. All samples have a flexural strength greater than 65 MPa after 60 days. CONCLUSION: The addition of partially silanized bioactive glasses allows for obtaining a material that releases ions over a longer period of time. CLINICAL SIGNIFICANCE: This type of material could be used as a denture base material, helping to preserve oral health by preventing the demineralization of the residual dentition through the release of appropriate ions that serve as substrates for hydroxyapatite formation.
- Publikační typ
- časopisecké články MeSH
This study aimed to prepare a bioactive acrylic material by adding different types of glasses. Commercially available polymerized acrylic resin was mixed with 10% of four different types of glasses in the powder form and cured. Flexural strength, sorption, and solubility of the samples were tested according to ISO 20795-1:2013. The total number of samples used in the tests were 60. The materials were placed in artificial saliva of pH 4 and 7, and elution was performed for 0, 1, 28, and 42 days. The collected samples were analyzed using inductively coupled plasma atomic emission spectrometry to detect Ca, P, and Si ions and using ion chromatography to detect F ions. The materials obtained after modification with glasses showed lower compressive strength compared with pure polymethyl methacrylate but met the standard requirements. Two glass types showed higher solubility values compared with the value defined by the ISO standard. Biomin C and S53P4 released Ca, P, and Si ions, respectively, after 42 days in artificial saliva. Acrylic resins modified with 10% Biomin C and S53P4 glasses can be a valuable source of Ca and P ions under acid conditions for 28 and 42 days.
The colonisation of the surface of removable acrylic dentures by various types of microorganisms can lead to the development of various diseases. Therefore, the creation of a bioactive material is highly desirable. This study aimed to develop a denture base material designed to release bioactive ions into the oral environment during use. Four types of bioactive glasses (BAG)-S53P4, Biomin F, 45S5, and Biomin C-were incorporated into the PMMA acrylic resin, with each type constituting 20 wt.% (10 wt.% non-silanised and 10% silanised) of the mixture, while PMMA acrylic resin served as the control group. The specimens were subsequently immersed in distilled water, and pH measurements of the aqueous solutions were taken every seven days for a total of 38 days. Additionally, surface roughness and translucency measurements were recorded both after preparation and following seven days of immersion in distilled water. The cytotoxicity of these materials on human fibroblast cells was evaluated after 24 and 48 h using Direct Contact and MTT assays. Ultimately, the elemental composition of the specimens was determined through energy-dispersive X-ray (EDX) spectroscopy. In general, the pH levels of water solutions containing BAG-containing acrylics gradually increased over the storage period, reaching peak values after 10 days. Notably, S53P4 glass exhibited the most significant increase, with pH levels rising from 5.5 to 7.54. Surface roughness exhibited minimal changes upon immersion in distilled water, while a slight decrease in material translucency was observed, except for Biomin C. However, significant differences in surface roughness and translucency were observed among some of the BAG-embedded specimens under both dry and wet conditions. The composition of elements declared by the glass manufacturer was confirmed by EDX analysis. Importantly, cytotoxicity analysis revealed that specimens containing BAGs, when released into the environment, did not adversely affect the growth of human gingival fibroblast cells after 48 h of exposure. This suggests that PMMA acrylics fabricated with BAGs have the potential to release ions into the environment and can be considered biocompatible materials. Further clinical trials are warranted to explore the practical applications of these materials as denture base materials.
- Publikační typ
- časopisecké články MeSH