Volumetric shrinkage (VS) of conventional, bulk-fill, and core build-up resin-based composites (RBCs) of various thickness (1-5 mm) was measured using the modified bonded-disk method with confocal laser scanning microscopy. Additionally, the bottom-to-top ratio of Vickers hardness (%VH) was measured. Conventional RBCs exhibited significantly higher VS than bulk-fill and core build-up RBCs (p<0.05). As specimen thickness increased, VS relative to volume (%VS) and difference in VS at each depth (VSdepth) decreased. For conventional RBCs, there was a significant drop in VSdepth between 1 mm and 2 mm (p<0.05), and another drop was observed between 3 mm and 4 mm (p<0.05) where %VH decreased below 90%. For bulk-fill and core build-up RBCs, VSdepth decreased significantly between 2 mm and 3 mm (p<0.05), but %VH exceeded 90% even in 5 mm deep cavities. These results indicated that post-curing contributed to lower shrinkage in deeper layers, and that conventional RBCs were not adequately polymerized at the depth of over 3 mm.
The color-matching ability of single-shade composites Omnichroma (OMN) and Omnichroma Flow (OCF) is ensured by structural color, which arises from monodisperse 260 nm spherical fillers. This study evaluated how filler load influences the color adjustment potential of composite restorations to human teeth of various shades. The performance of composites containing the 260 nm spherical fillers -OMN (79 wt%), OCF (71 wt%), and experimental composites R1 (65 wt%), and R2 (60 wt%)- was compared to two conventional A2-shade composites and a transparent composite. Additionally, the translucency parameter, spectral reflectance, and light transmission properties were assessed. Composites with a lower load of the 260 nm spherical fillers exhibited lower light diffusion and lower reflectance in the yellow-to-red range (580-650 nm), which is characteristic for the structural color of OMN and OCF. The best color adjustment was achieved with OCF, presumably due to its high translucency and uniform spectral reflectance.
- MeSH
- barva MeSH
- lidé MeSH
- složené pryskyřice * chemie MeSH
- testování materiálů MeSH
- Check Tag
- lidé MeSH
- Publikační typ
- časopisecké články MeSH
The recently introduced resin composites with a universal shade are claimed to match any tooth color. In this study, it was examined how composite thickness affects the color adjustment of conventional and universal-shade composites to background dentin. Thirty sound human central incisors of various shade were used, and color differences between their intact labial surfaces, exposed dentin surfaces and composite restorations (thickness 1-3 mm) were evaluated. In addition, the translucency, light transmission characteristics, and spectral reflectance of the composites were measured. The results showed that universal-shade composites outperformed conventional composites of A2 shade in the adjustment of hue and chroma (p<0.05) but not in lightness (p>0.05). The color adjustment potential of all composites significantly decreased as their thickness increased (p<0.05). The effect of thickness on Omnichroma and Omnichroma Flow was less marked, presumably because of their higher translucency (p<0.05) and structural coloration which induces light reflectance in the yellow-to-red range.
- MeSH
- barva MeSH
- dentin * MeSH
- lidé MeSH
- složené pryskyřice * chemie MeSH
- testování materiálů MeSH
- Check Tag
- lidé MeSH
- Publikační typ
- časopisecké články MeSH
This study investigated how the double application of adhesives and dentin moisture level influence the microtensile bond strength (μTBS) of universal adhesives containing different hydrophilic monomers to bur-cut dentin. Four universal adhesives (Scotchbond Universal, Clearfil Universal Bond Quick, Prime&Bond Universal, BeautiBond Universal) were applied to wet and dry bur-cut dentin either in one or two layers. The μTBS test was performed after 25,000 thermal cycles, and scanning electron microscopy was used for the analysis of failure mode and interfacial ultrastructure. Double application significantly improved μTBS on wet dentin (p<0.001), but the effect was not significant on dry dentin (p>0.050). Double application also enhanced the formation of resin tags and limited voids within the adhesive layer of BeautiBond Universal. Dentin moisture had a significant effect on μTBS only if the adhesives were applied in a single layer (p=0.007). Except for Prime&Bond Universal, the tested universal adhesives performed better on dry dentin.
This study investigated the influence of application/wash-out times of sodium hypochlorite (NaOCl) and hypochlorous acid (HOCl) on dentin bond strength of one-step self-etch adhesives (1-SEAs). Human coronal dentin discs with a standardized smear layer were pretreated with 6% NaOCl or 100 ppm HOCl for 5 s, 15 s, or 30 s, and washed out with water for 5 s, 15 s or 30 s with or without the application of Clearfil DC Activator (CDA). No pretreatment was used as a control. The discs were bonded with a 1-SEA (Bond Force II or Clearfil Universal Bond Quick) and microtensile bond strength (μTBS) was measured after 24 h. Pretreatment with NaOCl for 15 s and 30 s significantly decreased μTBS (p<0.05), irrespective of wash-out time. The application of CDA recovered μTBS but did not outperform the control group. Conversely, pretreatment with HOCl for 15 s and 30 s followed by 30 s wash-out time significantly increased μTBS of 1-SEAs (p<0.05), regardless of CDA application.
The effect of 1-week water storage and subsequent 10,000 thermal cycles on light transmission properties (straight-line transmission (G0), diffusion (DF), the amount of transmitted light (AV)), translucency parameter (TP) and refractive index (RI) of four nanofilled flowable composites was examined. The composites included Filtek Supreme Ultra Flowable Restorative (FSU), Estelite Flow Quick (EFQ), Estelite Universal Flow, (EUF), and Clearfil Majesty ES Flow (ESF), all of A3 shade. For composites with lower filler load (FSU, EFQ), water storage increased G0, AV and TP, but subsequent thermocycling decreased them. An opposite tendency was found for DF. Materials with higher filler load (EUF, ESF) were not significantly affected by aging conditions. RI of EFQ and EUF containing bisphenol A polyethoxy methacrylate (Bis-MPEPP) increased significantly after thermocycling. Additionally, morphological changes were observed using scanning electron microscopy which revealed cracks within nanocluster fillers and dislocation of particles in FSU and EFQ after thermocycling.
The effect of curing mode of dual-cure resin cements on the tensile bond strength (TBS) of universal adhesives to enamel, dentin, zirconia, lithium disilicate ceramics (LDS), feldspathic porcelain (FP), and a Pd-Au alloy was evaluated. The substrates were bonded using Tokuyama Universal Bond (TUB) or Scotchbond Universal Adhesive (SBU), followed by luting with Estecem II (ECII) or Rely-X Ultimate (RXU), respectively, which were used either in light-curing or self-curing mode. The TBS test was performed after 24 h or 5,000 thermal cycles. Light-curing significantly improved the 24-h TBS of TUB/ECII to enamel, dentin and FP, as well as the TBS of SBU/RXU to all substrates except LDS. After thermal cycling, light-curing significantly increased the TBS of both adhesives/cements to dentin, but significant differences between curing modes were seldom observed for other substrates. This suggested that light-curing is essential for the hydrophilic dentin, but self-curing might be sufficient for other substrates.
The effect of various pretreatments on the bonding of a resin cement to resin-composite CAD/CAM blocks (RCBs) was examined. The surface of dispersed-filler RCBs (DF-RCBs) and a polymer infiltrated ceramic network RCB (PICN-RCB) was roughened using hydrofluoric acid etching (HF) or sandblasting, and followed by silanization and/or universal adhesive (UA) application. Microtensile bond strength (µTBS), surface roughness parameters (arithmetical mean height (Sa); developed interfacial area ratio (Sdr)), and critical surface energy (γc) were determined. For most DF-RCBs, the highest µTBS was obtained using HF+UA. UA application to DF-RCBs resulted in similar or higher µTBS compared to silanization, which indicates that silane treatment is not crucial for DF-RCBs, especially after HF. In contrast, the highest µTBS to PICN-RCB was obtained with silanization. Both roughening pretreatments significantly increased the surface roughness parameters and the γc of all RCBs. The γc was positively correlated with Sa (r=0.756, p<0.001) and Sdr (r=0.837, p<0.001).
- MeSH
- keramika MeSH
- klinické protokoly MeSH
- kyselina fluorovodíková MeSH
- pevnost v tahu MeSH
- povrchové vlastnosti MeSH
- pryskyřičné cementy MeSH
- receptory interleukinů - společná gama-podjednotka MeSH
- silany MeSH
- složené pryskyřice MeSH
- testování materiálů MeSH
- vazba zubní * MeSH
- Publikační typ
- časopisecké články MeSH
The effect of warm air-blowing on the sealing ability of two one-bottle and one two-bottle silane-containing universal adhesives (UAs) applied to lithium disilicate ceramics (LDS) was evaluated. Tapered cavities prefabricated in LDS blocks (IPS e.max CAD) were treated by the adhesives, air-blown either with normal air (23±1°C) or warm air (60±5°C), and filled with a flowable resin composite. Interfacial gap formation was observed using swept-source optical coherence tomography immediately after filling, after 24 h, 5,000 and 10,000 thermal cycles, and an additional 1-year water storage. Specimens bonded using normal air-blown one-bottle UAs exhibited a significantly higher gap formation than the two-bottle UA (p<0.001), and detached within 24 h. Warm air-blowing significantly decreased the gap formation of one-bottle UAs (p<0.001), but the specimens dislocated within 24 h or during thermocycling. The two-bottle UA withstood all aging procedures and warm air-blowing significantly decreased its 1-year gap formation compared to normal air-blowing (p=0.002).
The effect of long-term water storage on the regional ultimate tensile strength (UTS), water sorption (Wsp) and water solubility (Wsl) of conventional and bulk-fill resin composites at various depths was investigated. Composite specimens light-cured from one side were sectioned into beams corresponding to different depths (1-5 mm) and stored in water for 24 h, 1 week, 1 month, 6 months or 1 year. UTS increased during the first week and then gradually decreased over time, especially in deeper regions. Bulk-fill composites initially exhibited similar UTS at all depths, whereas the UTS of conventional composites at 1 mm and 5 mm differed significantly at all time points. Wsp and Wsl increased with depth and storage time, markedly at 3-5 mm after 1 month for conventional composites and after 6 months for bulk-fill composites. The signs of degradation at depths beyond 3 mm suggested that even bulk-fill composites have suboptimal properties in layers more than 3 mm in thickness.
- MeSH
- pevnost v tahu MeSH
- polymerizace MeSH
- rozpustnost MeSH
- složené pryskyřice * MeSH
- testování materiálů MeSH
- voda * MeSH
- Publikační typ
- časopisecké články MeSH