The increasing incidence of trauma in medicine brings with it new demands on the materials used for the surgical treatment of bone fractures. Titanium, its alloys, and steel are used worldwide in the treatment of skeletal injuries. These metallic materials, although inert, are often removed after the injured bone has healed. The second-stage procedure-the removal of the plates and screws-can overwhelm patients and overload healthcare systems. The development of suitable absorbable metallic materials would help us to overcome these issues. In this experimental study, we analyzed an extruded Zn-0.8Mg-0.2Sr (wt.%) alloy on a rabbit model. From this alloy we developed screws which were implanted into the rabbit tibia. After 120, 240, and 360 days, we tested the toxicity at the site of implantation and also within the vital organs: the liver, kidneys, and brain. The results were compared with a control group, implanted with a Ti-based screw and sacrificed after 360 days. The samples were analyzed using X-ray, micro-CT, and a scanning electron microscope. Chemical analysis revealed only small concentrations of zinc, strontium, and magnesium in the liver, kidneys, and brain. Histologically, the alloy was verified to possess very good biocompatibility after 360 days, without any signs of toxicity at the site of implantation. We did not observe raised levels of Sr, Zn, or Mg in any of the vital organs when compared with the Ti group at 360 days. The material was found to slowly degrade in vivo, forming solid corrosion products on its surface.

• Klíčová slova
• absorbable metals, alloy accumulation, biocompatibility, in vivo, internal organs, magnesium, strontium, systemic reactions, toxicity, zinc,
• MeSH
• fraktury tibie * metabolismus   chirurgie   MeSH
• hořčík chemie   farmakokinetika   farmakologie   MeSH
• králíci MeSH
• lidé MeSH
• slitiny * chemie   farmakokinetika   farmakologie   MeSH
• stroncium chemie   farmakokinetika   farmakologie   MeSH
• testování materiálů * MeSH
• tibie metabolismus   patologie   MeSH
• vstřebatelné implantáty * MeSH
• zinek chemie   farmakokinetika   farmakologie   MeSH
• zvířata MeSH
• Check Tag
• králíci MeSH
• lidé MeSH
• zvířata MeSH
• Publikační typ
• časopisecké články MeSH
• Názvy látek
• hořčík MeSH
• slitiny * MeSH
• stroncium MeSH
• zinek MeSH

Degradable zinc-based alloys with an appropriate corrosion rate are promising materials for the preparation of temporary orthopaedic implants. Previously, we prepared and characterised a novel Zn1.5Mg alloy. This paper is focused on the characterisation of this alloy after a surface pre-treatment, which should mimic processes occurring in vivo. The samples of the Zn1.5Mg alloy were immersed in a simulated body fluid (SBF) at 37°C for 14days in order to form a protective layer of corrosion products. Thereafter, these samples were used for the corrosion rate determination, an indirect in vitro cytotoxicity test, as well as for a direct contact test and were compared with the non-treated samples. The protective layer was characterized by SEM and its chemical composition was determined by EDS and XPS analysis. The corrosion rate was significantly decreased after the pre-incubation. The protective layer of corrosion products was rich in Ca and P. The pre-incubated samples exhibited increased cytocompatibility in the indirect test (metabolic activity of L929 cells was above 70%) and we also observed osteoblast-like cell growth directly on the samples during the contact tests. Thus, the pre-incubation in SBF leading to improved cytocompatibility could represent more appropriate model to in vivo testing.

• Klíčová slova
• Biodegradable alloys, Cytocompatibility, In vitro testing, Zinc,
• MeSH
• buněčné linie MeSH
• hořčík * chemie   farmakologie   MeSH
• koroze MeSH
• myši MeSH
• osteoblasty cytologie   metabolismus   MeSH
• slitiny * chemie   farmakologie   MeSH
• tělesné tekutiny chemie   MeSH
• testování materiálů * MeSH
• viabilita buněk účinky léků   MeSH
• vstřebatelné implantáty * MeSH
• zinek * chemie   farmakologie   MeSH
• zvířata MeSH
• Check Tag
• myši MeSH
• zvířata MeSH
• Publikační typ
• časopisecké články MeSH
• Názvy látek
• hořčík * MeSH
• slitiny * MeSH
• zinek * MeSH

In this study, advanced techniques such as atom probe tomography, atomic force microscopy, X-ray photoelectron spectroscopy, and electrochemical impedance spectroscopy were used to determine the corrosion mechanism of the as-ECAPed Zn-0.8Mg-0.2Sr alloy. The influence of microstructural and surface features on the corrosion mechanism was investigated. Despite its significance, the surface composition before exposure is often neglected by the scientific community. The analyses revealed the formation of thin ZnO, MgO, and MgCO3 layers on the surface of the material before exposure. These layers participated in the formation of corrosion products, leading to the predominant occurrence of hydrozincite. In addition, the layers possessed different resistance to the environment, resulting in localized corrosion attacks. The segregation of Mg on the Zn grain boundaries with lower potential compared with the Zn-matrix was revealed by atom probe tomography and atomic force microscopy. The degradation process was initiated by the activity of micro-galvanic cells, specifically Zn - Mg2Zn11/SrZn13. This process led to the activity of the crevice corrosion mechanism and subsequent attack to a depth of 250 μm. The corrosion rate of the alloy determined by the weight loss method was 0.36 mm·a-1. Based on this detailed study, the degradation mechanism of the Zn-0.8Mg-0.2Sr alloy is proposed.

• Klíčová slova
• Biodegradable metals, Characterization, ECAP, Mechanism, Zinc-based alloy,
• Publikační typ
• časopisecké články MeSH

Metals are widely utilized as implant materials for bone fixtures as well as stents. Biodegradable versions of these implants are highly desirable since patients do not have to undergo a second surgery for the materials to be removed. Attractive options for such materials are zinc silver alloys since they also offer the benefit of being antibacterial. However, it is important to investigate the effect of the degradation products of such alloys on the surrounding cells, taking into account silver cytotoxicity. Here we investigated zinc alloyed with 1 % of silver (Zn1Ag) and how differently concentrated extracts (1 %-100 %) of this material impact human umbilical vein endothelial cells (HUVECs). More specifically, we focused on free radical generation and oxidative stress as well as the impact on cell viability. To determine free radical production we used diamond-based quantum sensing as well as conventional fluorescent assays. The viability was assessed by observing cell morphology and the metabolic activity via the MTT assay. We found that 1 % and 10 % extracts are well tolerated by the cells. However, at higher extract concentrations we observed severe impact on cell viability and oxidative stress. We were also able to show that quantum sensing was able to detect significant free radical generation even at the lowest tested concentrations.

• Klíčová slova
• Biodegradable zinc, Cytotoxicity, Free radical, NV center, Nanodiamond, Relaxometry,
• MeSH
• biokompatibilní materiály chemie   farmakologie   MeSH
• endoteliální buňky pupečníkové žíly (lidské) * účinky léků   MeSH
• lidé MeSH
• nanodiamanty * chemie   MeSH
• oxidační stres * účinky léků   MeSH
• slitiny * chemie   MeSH
• stříbro toxicita   chemie   MeSH
• testování materiálů metody   MeSH
• viabilita buněk * účinky léků   MeSH
• volné radikály metabolismus   MeSH
• vstřebatelné implantáty škodlivé účinky   MeSH
• zinek * MeSH
• Check Tag
• lidé MeSH
• Publikační typ
• časopisecké články MeSH
• Názvy látek
• biokompatibilní materiály MeSH
• nanodiamanty * MeSH
• slitiny * MeSH
• stříbro MeSH
• volné radikály MeSH
• zinek * MeSH

The aim of the research was to characterize the soldering alloy type Zn-Mg-Sr and direct the soldering of SiC ceramics with Cu-SiC-based composite. It was investigated whether the proposed composition of the soldering alloy was appropriate for soldering those materials at the defined conditions. For the determination of the solder melting point, TG/DTA analysis was applied. The Zn-Mg system is of the eutectic type with a reaction temperature of 364 °C. The effect of strontium on the phase transformation was minimal, owing to its lower content. The microstructure of the soldering alloy type Zn3Mg1.5Sr is formed of a very fine eutectic matrix containing segregated phases of strontium-SrZn13 and magnesium-MgZn2 and Mg2Zn11. The average tensile strength of the solder is 98.6 MPa. The tensile strength was partially increased by solder alloying with magnesium and strontium. The SiC/solder joint was formed due to the distribution of magnesium from the solder to the boundary with the ceramics at the formation of a phase. Owing to soldering in air, oxidation of the magnesium took place and the oxides formed were combined with the silicon oxides that remained on the surface of the ceramic material-SiC. Thus, a strong bond based on oxygen was obtained. An interaction between the liquid zinc solder and the copper matrix of the composite substrate took place at the formation of a new phase-γCu (Cu5Zn8). The shear strength was measured on several ceramic materials. The average shear strength of the combined SiC/Cu-SiC joint fabricated with Zn3Mg1.5Sr solder was 62 MPa. When soldering similar ceramic materials mutually, a shear strength of as much as around 100 MPa was observed.

• Klíčová slova
• Cu-SiC composite, SiC ceramics, Zn-Mg-Sr solder, soldering, ultrasonic soldering,
• Publikační typ
• časopisecké články MeSH

In this pilot study, we investigated the biocompatibility and degradation rate of an extruded Zn-0.8Mg-0.2Sr (wt.%) alloy on a rabbit model. An alloy screw was implanted into one of the tibiae of New Zealand White rabbits. After 120 days, the animals were euthanized. Evaluation included clinical assessment, microCT, histological examination of implants, analyses of the adjacent bone, and assessment of zinc, magnesium, and strontium in vital organs (liver, kidneys, brain). The bone sections with the implanted screw were examined via scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS). This method showed that the implant was covered by a thin layer of phosphate-based solid corrosion products with a thickness ranging between 4 and 5 µm. Only negligible changes of the implant volume and area were observed. The degradation was not connected with gas evolution. The screws were fibrointegrated, partially osseointegrated histologically. We observed no inflammatory reaction or bone resorption. Periosteal apposition and formation of new bone with a regular structure were frequently observed near the implant surface. The histological evaluation of the liver, kidneys, and brain showed no toxic changes. The levels of Zn, Mg, and Sr after 120 days in the liver, kidneys, and brain did not exceed the reference values for these elements. The alloy was safe, biocompatible, and well-tolerated.

• Klíčová slova
• alloy accumulation, bioabsorbable metals, biocompatibility, in-vivo biocompatibility, internal organs, magnesium, strontium, systemic reactions, toxicity, zinc,
• Publikační typ
• časopisecké články MeSH

Biodegradable materials are of interest for temporary medical implants like stents for restoring damaged blood vessels, plates, screws, nails for fixing fractured bones. In the present paper new biodegradable Zn-2Mg alloy prepared by conventional casting and hot extrusion was tested in in vitro and in vivo conditions. Structure characterization and mechanical properties in tension and compression have been evaluated. For in vivo tests, hemispherical implants were placed into a rat cranium. Visual observation of the living animals, an inspection of implant location and computed tomography CT imaging 12 weeks after implantation were performed. Extracted implants were studied using scanning electron microscopy (SEM) on perpendicular cuts through corrosion products. The behaviour of zinc alloy both in in vitro and in vivo conditions was compared with commercially used Mg-based alloy (Mg-4Y-3RE) prepared by conventional casting and hot extrusion. Both compressive and tensile yield strengths of Zn and Mg-based alloys were similar; however, the brittleness of Mg-4Y-3RE was lower. Zn and Mg-based implants have no adverse effects on the behaviour or physical condition of rats. Moreover, gas bubbles and the inflammatory reaction of the living tissue were not detected after the 12-week period.

• Klíčová slova
• biodegradable materials, corrosion, in-vivo tests, magnesium, zinc,
• Publikační typ
• časopisecké články MeSH

In vitro testing is the first important step in the development of new biomaterials. The human fetal osteoblast cell line hFOB 1.19 is a very promising cell model; however, there are vast discrepancies in cultivation protocols, especially in the cultivation temperature and the presence of the selection reagent, geneticin (G418). We intended to use hFOB 1.19 for the testing of Zn-based degradable metallic materials. However, the sensitivity of hFOB 1.19 to zinc ions has not yet been studied. Therefore, we compared the toxicity of zinc towards hFOB 1.19 under different conditions and compared it with that of the L929 mouse fibroblast cell line. We also tested the cytotoxicity of three types of Zn-based biomaterials in two types of media. The presence of G418 used as a selection reagent decreased the sensitivity of hFOB 1.19 to Zn2+. hFOB 1.19 cell line was more sensitive to Zn2+ at elevated (restrictive) temperatures. hFOB 1.19 cell line was less sensitive to Zn2+ than L929 cell line (both as ZnCl2 and extracts of alloys). Therefore, the appropriate cultivation conditions of hFOB 1.19 during biomaterial testing should be chosen with caution.

• Klíčová slova
• hFOB 1.19 osteoblasts, in vitro cytotoxicity testing, zinc degradable materials,
• Publikační typ
• časopisecké články MeSH

Zinc-based alloys represent one of the most highly developed areas regarding biodegradable materials. Despite this, some general deficiencies such as cytotoxicity and poor mechanical properties (especially elongation), are not properly solved. In this work, a Zn-5Mg (5 wt.% Mg) composite material with tailored mechanical and superior corrosion properties is prepared by powder metallurgy techniques. Pure Zn and Mg are mixed and subsequently compacted by extrusion at 200 °C and an extrusion ratio of 10. The final product possesses appropriate mechanical properties (tensile yield strength = 148 MPa, ultimate tensile strength = 183 MPa, and elongation = 16%) and decreased by four times the release of Zn in the initial stage of degradation compared to pure Zn, which can highly decrease cytotoxicity effects and therefore positively affect the initial stage of the healing process.

• Klíčová slova
• biomaterials, metallic composites, powder technology, zinc,
• Publikační typ
• časopisecké články MeSH